Boron Effect on Microstructure, Superplastic Behavior, and Mechanical Properties of Ti-4Al-3Mo-1V Alloy

The microstructure evolution, superplasticity, and room temperature mechanical properties of Ti-4%Al-1%V-3%Mo alloys modified with 0.01-2 wt.% boron were investigated. Increasing the boron content from 0 to 0.1 wt.% effectively refined prior β-grains, reducing a mean grain size from ~700 µm to ~210 µm. Whiskers of the TiB phase with a size in a range of 0.7-2.9 µm were observed after solidification and thermomechanical processing. Alloys with 0.01-0.1 wt.% boron exhibited similar superplastic elongations and strain rate sensitivity coefficient m of 0.4-0.5 at a strain rate of 1×10-3 s-1 and the elongation to failure decreased from 1000% at 875°С to 400-500% at 700°С. Along with this, the minor boron addition effectively decreased flow stress values, especially at 775 °C, that was explained by the acceleration of the recrystallization and globularization of the microstructure at the initial stage of deformation. Recrystallization-induced decrease in yield strength from 770 MPa to 680 MPa was observed with an increase in boron content from 0 to 0.1 wt.%. Heat treatment increased post-forming strength characteristics for the alloys with 0.01-0.1 wt.% boron by 90–140 MPa without ductility reduction. Alloys with 1-2 wt.% B demonstrated the opposite behavior. The grain refinement effect was not revealed, and prior β grain sizes were ~670-750 µm after solidification. Thermomechanical processing promoted the fragmentation of boride whiskers and the formation of near-spherical particles with a size of ~1 μm for the alloy with a eutectic concentration of 2 wt.% B. A high fraction of borides, ~5-11%, in the alloys with 1-2 wt.% B deteriorated the superplastic properties and drastically decreased ductility at room temperature. The alloy with 2 wt.% B demonstrated non-superplastic behavior and a low level of mechanical properties, meanwhile, the alloy with 1% boron exhibited high-temperature superplasticity at 875 °C with elongation of ~500%, and yield strength of 830 MPa, ultimate tensile strength of 1020 MPa at a room temperature after 100% of superplastic deformation.