Structure, Electrical Properties, and Thermal Stability of the Mn/Nb Co-Doped Aurivillius-Type Na0.5Bi4.5Ti4O15 High Temperature Piezoelectric Ceramics

In order to meet the urgent need for high temperature piezoelectric materials with a Curie temperature over 400 degrees C, the Mn/Nb co-doped strategy has been proposed to improve the weak piezoelectric performance of the Aurivillius-type Na0.5Bi4.5Ti4O15 (NBT) high temperature piezoelectric ceramics. In this paper, the crystal structure, electrical properties, and thermal stability of the B-site Mn/Nb co-doped Na0.5Bi4.5Ti4-x(Mn1/3Nb2/3)(x)O-15 (NBT-100x) ceramics were systematically investigated by the conventional solid-state reaction method. The crystal structural analysis results indicate that the NBT-100x ceramics have typical bismuth oxide layer type phase structure and high anisotropic plate-like morphology. The lattice parameters and the grain sizes increase with the B-site Mn/Nb co-doped content. The electrical properties were significantly improved by Mn/Nb co-doped modifications. The maximum of the piezoelectric coefficient d(33) was found to be 29 pC/N for the NBT-2 ceramics, nearly twice that of the unmodified NBT ceramics. The highest values of the planar electromechanical coupling factor k(p) and thickness electromechanical coupling factor k(t) were also obtained for the NBT-2 ceramics, at 5.4% and 31.2%, respectively. The dielectric spectroscopy showed that the Curie temperature Tc of the Mn/Nb co-doped NBT-100x ceramics is slightly higher than that of unmodified NBT ceramics (646 degrees C). The DC resistivity of the NBT-2 ceramics is higher than 10(6) omega center dot cm at 500 degrees C. All the results together with the good thermal stability demonstrated the Mn/Nb co-doped ceramics as an effective method to improve the NBT based piezoelectric ceramics and the potential candidates of the Mn/Nb co-doped NBT-100x ceramics for high temperature piezoelectric applications.