Dynamic Recrystallization Kinetics of As-Cast Fe-Cr-Al-La Stainless Steel During Hot Deformation

To investigate the dynamic recrystallization (DRX) behavior of as-cast Fe-20Cr-5.5Al-0.64La stainless steel, a series of compression tests were carried out on a Gleeble-3500 thermal simulator in the temperature range of 1000~1150 °C and the strain rate range of 0.001~1 s−1. The true stress-true strain curves were obtained and their characteristics were analyzed. Using regression analysis, the apparent activation energy for the Fe-20Cr-5.5Al-0.64La stainless steel was estimated to be 300.19 kJ/mol, and the constitutive equation was developed successfully with a hyperbolic sine equation as: ε˙=e21.91sinh⁡0.035σ3.18exp⁡−300190RT. The critical strain, the peak strain and the strain for the maximum softening rate were identified based on the work hardening rate curves and expressed as a function of the Zener−Hollomon parameter. The kinetic model of DRX was established using the stress−strain data. According to the analysis of the kinetics model and microstructure evolution, the evolution of DRX volume could be described as follows: the volume fraction of DRX grains increased with an increase in strain; at a fixed deformation temperature, the DRX volume fraction was larger at a lower strain rate for the same strain; and the size of DRX grains increased with an increase in temperature or a decrease in strain rate.