Excellent Energy-Storage Performance of (0.85-x)NaNbO3-xNaSbO3-0.15(Na0.5La0.5)TiO3 Antiferroelectric Ceramics through B-Site Sb5+Driven Phase Transition

NaNbO3-based relaxor antiferroelectric (AFE) ceramics are receiving more and more attention for high power pulse applications. A commonly used design strategy is to add complex perovskites with lower tolerance factors. Herein, a new lead-free AFE system of (0.85 - x)NaNbO3-xNaSbO3-0.15(Na0.5La0.5)TiO3 was specially designed considering the substitution of Sb5+ for Nb5+ reduces the polarizability of B-site ions but increases the tolerance factor. The formation of nanodomains with stable AFE orthorhombic R phase symmetry contributes to a slim and double-like polarization field hysteresis loop, while the increased resistivity and activation energy as a result of sintering aids lead to an enhanced breakdown strength. Therefore, an excellent energy density Wrec approximate to 6.05 J/cm3, a high energy efficiency eta approximate to 80.5%, and good charge-discharge performances (power density PD approximate to 155 MW/cm3 and discharging rate t0.9 approximate to 44.6 ns) were achieved in MnO2-doped x = 0.03 ceramics. The experimental results demonstrate that the B-site Sb5+ driven orthorhombic P-R phase transition and increased local structure disorder should provide a new strategy to design highperformance NaNbO3-based relaxor AFE capacitors.