Quantitative monitoring of impact damage to composite structures using blade coated MXene sensors

Low velocity impacts usually cause invisible damage of composite structure，which is hard to be found and will cause catastrophic failure. In this work, the blade-coated MXene sensor was used to monitor impact damage of composite laminates. For the purpose of impact monitoring, an experiment was designed where composite laminates were subjected to controlled energy impacts. A circular sensor with a diameter of 100 mm was arranged on the back of the laminate. And ultrasonic C-scan was used to examine delamination damage of laminates after each impact. The experimental results show that the sensor identifies the onset of impact and the generation of damage. And the relative resistance changes of the sensor have a directly linear proportional relationship to the delamination size. There is also a functional relationship between the electrical response of the sensor and the impact energy. The findings are of great significance for the application of composite structure, and can effectively avoid the safety hazards caused by invisible impact delamination damage.