Determination of the crystalline size of hexagonal La1-xSrxMnO3 (x=0.3) nanoparticles from X-ray diffraction - a comparative study

The electronic, magnetic, optical and elastic properties of nanomaterials are governed partially by the crystallite size and crystal defects. Here, the crystalline size of hexagonal La1-xSrxMnO3 (x = 0.3) nanoparticles was determined using various methods. Single-phase La0.7Sr0.3MnO3 nanopowders were produced after 10 h of milling in a commercial high-energy SPEX 8000D shaker mill, and then they were heated at 700 & DEG;C and 800 & DEG;C to study the effect of calcined temperature on the crystallization of nanoparticles. The modified Scherrer, Williamson-Hall, size-strain, and Halder-Wagner methods were used to determine the crystallite sizes and the elastic properties, such as intrinsic strain, stress, and energy density, from the X-ray diffraction peak broadening analysis. The obtained results were then compared with one another. The difference in crystallite sizes calculated from the different methods was due to the different techniques.