Determination of Interaction Parameters Between Mn and Al and the Influence of Mn on Al2O3 Inclusions Formation in High Mn and Al Content Fe-Mn-Al-O Melts at 1873 K

Metals(2023)

引用 0|浏览11
暂无评分
摘要
For the purpose of determining the interaction parameters between Mn and Al, and the influence of Mn on Al2O3 inclusions formation in the Fe-Mn-Al-O melts with high Mn and Al contents, three groups of Fe-Mn-Al-O melts with the initial Al content of 3, 5, and 7 mass% and different Mn contents were equilibrated with pure solid Al2O3 in an Al2O3 crucible at 1873 K and Ar-H2 atmosphere. Then, the interaction parameters between Mn and Al were deduced using the WIPF (Wagner’s Interaction Parameter Formalism) and the R-K polynomial (Redlich-Kister type polynomial), respectively. From the WIPF, the first- and second-order interaction parameters, eAlMn and rAlMn, were determined to be 0.0292 and −0.00016, respectively. From the R-K polynomial, the binary interaction parameters, ΩMn-Al0 and ΩMn-Al1, were determined to be 73,439 J/mol and −34,919 J/mol, respectively. The applicability of the WIPF to high Mn and Al content Fe-Mn-Al-O melts was investigated by comparing the Al activity calculated by the WIPF and the R-K polynomial using the obtained data. The results showed that WIPF can be used in high Mn and Al content melts in the current concentration range. Further from the iso-activity contours of Al, the activity of Al increases with increasing Al or Mn content. Finally, the thermodynamic calculations show that the addition of Mn decreases the equilibrium O content at the same Al content, making the formation of Al2O3 inclusions easier.
更多
查看译文
关键词
Fe-Mn-Al-O melt,high Mn and Al content,interaction parameter,Al-O equilibrium,Al2O3 inclusion
AI 理解论文
溯源树
样例
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要