Fabrication of Multifunctional Bio-Macromolecule Organic-Inorganic Hybrid System for Protein Silk: Photochromic, UV Protection, Fire-Proof and Super Durability.

Nowadays, high value-added and multifunctional textiles have attracted widespread attention due to the changing demands of modern life. This study focused on the fabrication of silk with photochromism, flame retardancy, UV resistance and durability using riboflavin sodium phosphate (RSP) and various metal ions (Fe2+, Fe3+, Al3+, and Ti4+). Attractively, the photochromic performance was one of the most distinctive features of the modified silk, and the yellow silk fabric turned into fluorescent green under UV lamp. After a detailed comparison, it was determined that RSP/Fe3+ hybrid system was most effective in improving anti-UV performance of the silk with a high UPF of 25.8, achieving a "Good" level of UV protection. Specifically, it achieved a B1 fire protection with a low damaged-length of 9.4 cm and a high LOI of 28.3 %. Additionally, the modified silk showed the lowest smoke density, reducing by approximately 84.1 % versus that of pristine silk. Moreover, the modified silk was able to meet the B1 classification and the "Good" UV protection requirements even after 75 washing cycles, making it more durable than most functional textiles reported. The further analysis indicated that RSP and metal ions can synergistically enhance the condensed-phase action, thereby improving the fire resistance of silk.