Calcium oxide nanoparticles: Biosynthesis, characterization and photocatalytic activity for application in yellow tartrazine dye removal

Dyes are substances that have a high polluting potential, due to their low biodegradability and chemical stability, causing serious environmental damage when disposed of incorrectly. Yellow tartrazine (YT) dye as an environmental liability requires attention, since it causes toxic effects in fish (Danio rerio) with a potential allergic effect in humans. In this context, the present study aims to synthesize and characterize calcium oxide nano particles (CaO-NPs) to evaluate the photocatalytic activity for the YT photodegradation under visible irradiation. CaO-NPs were synthesized by the biosynthesis method from golden linseed (Linum usitatissimum L.) extract. Central Composite Rotational Design (CCRD 2(3)) was used to determine the ideal condition for the photocatalytic tests. X-ray diffraction (XRD), zeta potential (ZP), physical adsorption of N-2, zero charge point (pH(zcp)), Attenuated Total Reflectance Fourier Transform Infrared Spectroscopy (ATR-FTIR), Scanning Electron Microscopy by Energy Dispersive Spectroscopy (SEM-EDS), Diffuse Reflectance Spectroscopy (DRS) and Field Emission Gun - Scanning Electron Microscope (FEG-SEM) were used to the CaO-NPs characterization. Thus, CaO-NPs presented S-BET = 14 +/- 0.02 m(2)g(-1), Dp = 20.9 +/- 0.02 nm and Vp = 0.054 +/- 0.004 cm(3)g(-1), characteristic of a mesoporous material. ATR-FTIR spectrum showed characteristic stretches of specific functional groups (-CH, -CO, C = C, Ca O, -OH) from plant extract and metallic precursor. CaO-NPs showed pHZCP equal to 7.74, positive surface charge (+12.7 mV) and bang gap energy of 2.61 eV. FEG-SEM micrographs showed that has a small agglomeration with defined morphology, but with irregular particle size (around 48 nm), and SEM-EDS micrographs showed an elemental composition (in weight) of the 50.24% oxygen, 3.32% magnesium, 2.29% iron, 10.44% calcium, 14.07% silicon, 3.33% aluminum and 0.63% potassium. Regarding CCRD 2(3), the ideal condition was the pH = 7.0, [CaO-NPs] = 1.2 g/L and [YT] = 20 mg/L, with 76.2% of photodegradation and a pseudo first-order reaction specific reaction rate k = 0.089 min(-1). After V cycles of CaO-NPs recycling, there was a decrease of around 22.83%, indicating a saturation of the active sites available in the nanocatalyst Therefore, CaO-NPs showed potential application for TY photodegradation to be used in wastewater treatment being an alternative nano-catalyst, meeting nanotechnology and sustainable development.