Highly Stable Amide-Functionalized Zirconium-Organic Frameworks: Synthesis, Structure, and Methane Storage Capacity

With the development of crystalline porous materials toward methane storage, the stability issue of metal-organic framework (MOF) materials has caused great concern despite high working capacity. Considering the high stability of zirconium-based MOFs and effective functions of amide groups toward gas adsorption, herein, a series of UiO-66 type of Zr-MOFs, namely, Zr-fcu-H/F/CH3/OH, were successfully designed and synthesized by virtue of amide-functionalized dicarboxylate ligands bearing distinct side groups (i.e., -H, -F, -CH3, and -OH) and ZrCl4 in the presence of trifluoroacetic acid as the modulator. Single-crystal X-ray diffraction and topology analyses reveal that these compounds are archetypal fcu MOFs encompassing octahedral and tetrahedral cages, respectively. The N-2 sorption isotherms and acid-base stability tests demonstrate that the materials possess not only relatively high surface areas, pore volumes, and appropriate pore sizes but also great hydrolytic stabilities ranging pH = 3-11. Furthermore, the volumetric methane storage working capacities of Zr-fcu-H, Zr-fcu-F, Zr-fcu-CH3, and Zr-fcu-OH at 298/273 K and 80 bar are 187/217, 175/193, 167/187, and 154/171 cm(3) (STP) cm(-3), respectively, which indicate that the zirconium-based crystalline porous materials are capable of storing relatively high amounts of methane.