Mechanical and plasma ablation properties of double-interface fibrous ZrB2-SiC ceramics for ultra-high-temperature application
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY(2024)
摘要
Double-interface fibrous ZrB2-SiC ceramics (DZSw) were prepared by wet-spinning and hot-pressing. The introduction of double-interface layers improves the interface bonding and crack tolerance making the bending strength and toughness of DZSw increased to 607 MPa and 6.3 MPa m1/2, respectively. After ablation testing in 9.34 MW/m2 plasma flame, DZSw remained intact, with linear and mass ablation rates of 0.3 mu m s-1 and 0.11 mg s-1, respectively. However, single-interface fibrous ZrB2-SiC ceramic (SZSw) produced penetrating cracks, so DZSw presented high ablation resistance than SZSw. The introduction of a dense ZrB2-SiC outer interface layer in DZSw interrupts the three-dimensional connected structure of the porous SiCw interface layer in SZSw and consequently reduces the oxygen diffusion rate of the ceramics. Moreover, the high emissivity and thermal conductivity enable DZSw to serve in the high heat flux ablation environment caused by faster flight speed.
更多查看译文
关键词
Double-interface,Fibrous ceramic,Plasma flame,Ablation resistance,Thermal conductivity
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要