Novel rich aromatic and phosphorus-containing compound cured epoxy resins toward outstanding comprehensive performances

Epoxy resin (EP) is quite flammable, which limits its application in areas such as coatings and electronic and electrical materials. In this study, 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DOPO) (or diphenylphosphine oxide (DPO)) 3-cyclohexene-1-formaldehyde (CC) and 4,4'diaminodiphenylmethane (DDM) were selected for the synthesis of two rich aromatic and phosphorus-containing compounds (DOPO-CC and DPO-CC). DOPO-CC and DPO-CC were introduced into epoxy pre-polymers to prepare epoxy thermosets with flame retardancy. When 5 wt% DOPO-CC (P content of 0.50 wt%) or DPO-CC (P content of 0.52 wt%) was added, the LOI values of the epoxy thermosets increased from 25.5% (pure EP) to 33.5% (EP added DOPO-CC) and 31.0% (EP added DPO-CC), respectively, and these epoxy thermosets also achieved the UL-94 V-0 rating. Additionally, cone calorimeter tests showed that the peak heat release rate (PHRR) and total heat release (THR) of epoxy thermoset containing 5 wt% DPO-CC reduced by 42.0% and 39.7% compared to those of pure EP, respectively. By reducing the thermal degradation rate (condensed phase) and combining and quenching free radicals (gaseous phase), the introduction of DOPO-CC or DPO-CC can efficiently improve the flame retardancy of epoxy thermosets. More importantly, the epoxy thermosets containing DOPO-CC or DPO-CC exhibited better mechanical properties than pure EP, which could be proven by the storage modulus and tensile strength. This study provided a new class of rich aromatic and phosphorus-containing compounds that can serve as co-curing agents for epoxy thermosets with outstanding comprehensive performances.