Well-Dispersed Bi nanoparticles for promoting the lithium storage performance of Si Anode: Effect of the bridging Bi nanoparticles

Silicon (Si) is considered a promising anode material for lithium-ion batteries (LIBs) due to its high theoretical specific capacity of up to 4200 mAh/g. However, the poor cycling and rate performances of Si induced by the low intrinsic electronic conductivity and large volume expansion during the lithiation/delithiation process limit its practical application. Herein, a novel silicon/bismuth@nitrogen-doped carbon (Si/Bi@NC) composite with nanovoids was synthesized and investigated as an advanced anode material for LIBs. In such a structure, ultrafine bismuth nanoparticles coupled with an N-doped carbon layer were introduced to modify the surface of Si nanoparticles. Subsequently, the lithiated LixBi has excellent high ionic conductivity and acts as a fast transport bridge for lithium ions. The introduced carbon coating layer and nanovoids can buffer the volume expansion of Si during the lithiation/ delithiation process, thus maintaining structural stability during the cycling process. As a result, the Si/Bi@NC composite exhibits excellent electrochemical performance, providing a relatively high capacity of 955.8 mAh/g at 0.5 A/g after 450 cycles and excellent rate performance with a high capacity of 477.8 mAh/g even at 10.0 A/g. Furthermore, the assembled full cell with LiFePO4 as cathode and pre-lithium Si/Bi@NC as anode can provide a high capacity of 138.8 mAh/g at 1C after 90 cycles, exhibiting outstanding cycling performance.