Preparation of Preformed Submicron Crosslinked Polymer Coils for Conformance Control in Low-Permeability Reservoirs

With the increasing development of low-permeability reservoirs, the significance of conformance control treatment has risen considerably. To address the conflict between injectability and plugging performance, as well as to enhance the deep migration capacity of conformance control agents, preformed submicron crosslinked polymer coils (SCPCs) have been manufactured using aqueous solution dispersion polymerization. Fourier transform infrared and scanning electron microscopy were employed to examine the chemical structure and micromorphology, while particle size distribution, zeta potential, rheological, and filtration properties were analyzed. The effectiveness of conformance control was confirmed through the parallel core displacement. The effective particle size of SCPCs was at a submicron level (500 similar to 800 nm). SCPCs exhibit a transitional threshold concentration between gel and sol states (0.25 wt%similar to 0.5 wt%). SCPCs can efficiently block the 1.2 mu m microporous filter membrane. The filtration time is up to 67.8 min. SCPCs can improve the water absorption rate of lower permeability cores from 21.21% to 57.89% with a permeability difference of 5. Therefore, SCPCs have good injectability, plugging performance, and deep migration capacity and can be used for conformance control in low-permeability reservoirs.