Synthesis and enhanced room-temperature thermoelectric properties of CuO-MWCNT hybrid nanostructured composites

This work presents the synthesis of novel copper oxide-multiwalled carbon nanotube (CuO-MWCNT) hybrid nanostructured composites and a systematic study of their thermoelectric performance at near-room temperatures as a function of MWCNT wt% in the composite. The CuO-MWCNT hybrid nanostructured composites were synthesized by thermal oxidation of a thin metallic Cu layer pre-deposited on the MWCNT network. This resulted in the complete incorporation of MWCNTs in the nanostructured CuO matrix. The thermoelectric properties of the fabricated CuO-MWCNT composites were compared with the properties of CuO-MWCNT networks prepared by mechanical mixing and with the properties of previously reported thermoelectric [CuO]99.9[SWCNT]0.1 composites. CuO-MWCNT hybrid composites containing MWCNTs below 5 wt% showed an increase in the room-temperature thermoelectric power factor (PF) by similar to 2 times compared with a bare CuO nanostructured reference thin film, by 5-50 times compared to mixed CuO-MWCNT networks, and by similar to 10 times the PF of [CuO]99.9[SWCNT]0.1. The improvement of the PF was attributed to the changes in charge carrier concentration and mobility due to the processes occurring at the large-area CuO-MWCNT interfaces. The Seebeck coefficient and PF reached by the CuO-MWCNT hybrid nanostructured composites were 688 mu V K-1 and similar to 4 mu W m-1 K-2, which exceeded the recently reported values for similar composites based on MWCNTs and the best near-room temperature inorganic thermoelectric materials such as bismuth and antimony chalcogenides and highlighted the potential of CuO-MWCNT hybrid nanostructured composites for applications related to low-grade waste heat harvesting and conversion to useable electricity. Novel copper oxide-multiwalled carbon nanotube hybrid nanostructured composites showed a high Seebeck coefficient (similar to 700 mu V K-1) and power factor (similar to 4 mu W m-1 K-2), exceeding the values reported for the state-of-the-art counterparts.