Facile fabrication of fluorine-free waterproof and breathable nanofiber membranes with UV-resistant and acid-alkali resistant performances

Membranes with good waterproofness and breathability are desired for the preparation of outdoor sports garments. However, current waterproof and breathable membranes use environmentally hazardous fluorinecontaining raw materials and suffer from many problems such as complicated preparation processes and single function. Therefore, it is a great challenge to select environmentally friendly raw materials to prepare multifunctional membranes with waterproof-breathable performance by simple preparation method. In this paper, fluorine-free poly(styrene-b-butadiene-b-styrene) (SBS), polyurethane (PU), and 2-hydroxy-4-n-octyloxy benzophenone (UV531) were selected to prepare multi-functional nanofiber membranes by convenient one-step electrospinning. The properties of the environmentally friendly multi-functional SBS/PU/UV531 nanofiber membranes were systematically optimized by adjusting the concentration of UV531 in the nanofiber membranes. The ultimately obtained multi-functional SBS/PU/UV531-2 nanofiber membrane shows excellent waterproofness (hydrostatic pressure: 58.8 kPa), high breathability (WVT rate: 5.2 kg m(-2) d(-1)), good mechanical properties (breaking strength: 7.26 MPa, breaking elongation: 327.9%), excellent UV resistance (UPF: 238.23), and strong acid and alkali resistance properties. This multi-functional nanofiber membrane has broad application prospects in a variety of fields such as outdoor protective clothing, extreme environment materials, and military products.