Improvement of Superconducting Joint Properties for GdBa₂Cu₃O_x Bulk Superconductors Joined with ErBa₂Cu₃O_x Superconductor Using Local Melt-Growth Method

The important factors in obtaining a high-quality superconducting joint were investigated for the superconducting joint of a GdBa2Cu3Ox (GdBCO) bulk superconductor with sintered ErBa2Cu3Ox (ErBCO) using the local melt-growth method. REBCO (RE: rare earth) bulk superconductors can be used as strong magnets by magnetizing them, but they require large bulk sizes for their application. Although the superconducting joint presents a viable solution, many possibilities for property improvement remain, such as property degradation, depending on the joining direction. By varying the joining thermal conditions and confirming the elemental distribution, magnetization properties near the joined part and the effects of these on the joining properties are clarified, and a method for fabricating high-performance joined samples is obtained. Microstructure segregation was rarely observed at the center of the joined part regardless of the joining direction, and the superconducting properties were negligible and small. The J(c)-B results are almost identical to those of the GdBCO matrix at a low field, confirming that the joined part minimally interferes with the superconducting current. Furthermore, by lowering the maximum temperature, shortening the holding time at the maximum temperature, and increasing the cooling rate, the region of mutual solid solution was reduced, and the J(c)-B under the self-magnetic field was enhanced. These results contribute to the development of the superconducting joining method, a critical aspect of larger bulk superconductors.