A Low-Temperature SiO₂ Interfacial Layer Preparation using Rapid Thermal Oxidation Process for GAA Nanosheet Based I/O Transistor

In this paper, a low-temperature SiO(2 )interfacial layer preparation using rapid thermal oxidation (RTO) process for gate-all-around (GAA) nanosheet (NS) based input-output (I/O) transistor is explored in detail. After preparing high-quality thick SiO2 IL at 600celcius, its MOS capacitor with W/TiN/HfO2/SiO2/Si substrate structure achieves well behaved multi-frequency capacitance-voltage characteristics, low leakage current, low interfacial trap density (Dit), and excellent time-dependent dielectric breakdown. For instance, its gate leakage under flatband voltage (V-fb)( -1) V is only 2.48 x 10(-9) A/cm(2), its minimum D-it reaches 5.1 x 10(10) eV(-1) cm(-2), and its ten-year lifetime effective voltage can reach 3.62 V at a failure rate of 0.01%. Moreover, a GAA NS based I/O device with a healthy gate stack is successfully prepared using this low-temperature SiO2 interfacial layer and its gate leakage is below 1 x 10-13 A, approaching the detection limit. These above results indicate that this low-temperature RTO-grown SiO2 IL has excellent quality and can meet the requirements of GAA NSs I/O transistors.