Adsorption of high-temperature CO2 by Ca2+/Na+-doped lithium orthosilicate: characterization, kinetics, and recycle

High-temperature solid adsorbent Li4SiO4 has received broad attention due to its high theoretical adsorption capacity, high regeneration capacity, and wide range of raw materials for preparation. In this paper, a Li4SiO4 adsorbent was prepared by MCM-48 as the silica precursor and modified by doping with metal ions (Ca2+ and Na+) for high-temperature capture of low-concentration CO2. The results showed that the surface of the Ca-doped (or Na-doped) Li4SiO4 adsorbent developed some particles that are primarily composed by Li2CaSiO4 (or Li3NaSiO4). Furthermore, the grains of the adsorbents became finer, effectively increasing the specific surface area and enhancing adsorption performance. Under 15 vol