High strength mullite-bond SiC porous ceramics fabricated by digital light processing
JOURNAL OF ADVANCED CERAMICS(2024)
摘要
Fabricating SiC ceramics via the digital light processing (DLP) technology is of great challenge due to strong light absorption and high refractive index of deep-colored SiC powders, which highly differ from those of resin, and thus significantly affect the curing performance of the photosensitive SiC slurry. In this paper, a thin silicon oxide (SiO2) layer was in-situ formed on the surface of SiC powders by pre-oxidation treatment. This method was proven to effectively improve the curing ability of SiC slurry. The SiC photosensitive slurry was fabricated with solid content of 55 vol% and viscosity of 7.77 Pa center dot s (shear rate of 30 s(-1)). The curing thickness was 50 mu m with exposure time of only 5 s. Then, a well-designed sintering additive was added to completely convert low-strength SiO2 into mullite reinforcement during sintering. Complex-shaped mullite-bond SiC ceramics were successfully fabricated. The flexural strength of SiC ceramics sintered at 1550 degrees C in air reached 97.6 MPa with porosity of 39.2 vol%, as high as those prepared by spark plasma sintering (SPS) techniques.
更多查看译文
关键词
digital light processing (DLP),SiC ceramics,pre-oxidation,mullite-bond SiC,mechanical properties
AI 理解论文
溯源树
样例
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要