Sequentially Processed Bulk-Heterojunction-Buried Structure for Efficient Organic Solar Cells with 500 nm Thickness.

Large-area printing fabrication is a distinctive feature of organic solar cells (OSCs). However, the advance of upscalable fabrication is challenged by the thickness of organic active layers considering the importance of both exciton dissociation and charge collection. In this work, a bulk-heterojunction-buried (buried-BHJ) structure is introduced by sequential deposition to realize efficient exciton dissociation and charge collection, thereby contributing to efficient OSCs with 500 nm thick active layers. The buried-BHJ distributes donor and acceptor phases in the vertical direction as charge transport channels, while numerous BHJ interfaces are buried in each phase to facilitate exciton dissociation simultaneously. It is found that buried-BHJ configurations possess efficient exciton dissociation and rapid charge transport, resulting in reduced recombination losses. In comparison with traditional structures, the buried-BHJ structure displays a decent tolerance to film thickness. In particular, a power conversion efficiency of 16.0% is achieved with active layers at a thickness of 500 nm. To the best of the authors' knowledge, this represents the champion efficiency of thick film OSCs.