Study on the microstructure and mechanical properties of VW73B alloy at high extrusion ratio

Abstract The microstructure and mechanical characteristics of VW73B prepared by a high extrusion ratio (70:1) were studied. High-strength plastic VW73B alloy containing long-period structural phase (LPSO) was obtained by extrusion process. OM, SEM, TEM, and EBSD were used to investigate the relationship between microstructure and mechanical characteristics of VW73B. The findings indicate that VW73B presents complete dynamic recrystallization after deformation, and there are 14H-LPSO phases, SFs, and a large amount of β´ phase, which are precipitated after aging treatment. The UTS, YS, and EL of VW73B in peak aging state are 406 MPa, 339 MPa, and 9%, respectively. The β´ phase, LPSO phase, poor texture, and fine grain strengthening of VW73B contribute to its exceptional characteristics.