Scalable Synthesis of High-Quality Ultrathin Ferroelectric Magnesium Molybdenum Oxide

The development of ultrathin, stable ferroelectric materials is crucial for advancing high-density, low-power electronic devices. Nonetheless, ultrathin ferroelectric materials are rare due to the critical size effect. Here, a novel ferroelectric material, magnesium molybdenum oxide (Mg2Mo3O8) is presented. High-quality ultrathin Mg2Mo3O8 crystals are synthesized using chemical vapor deposition (CVD). Ultrathin Mg2Mo3O8 has a wide bandgap (approximate to 4.4 eV) and nonlinear optical response. Mg2Mo3O8 crystals of varying thicknesses exhibit out-of-plane ferroelectric properties at room temperature, with ferroelectricity retained even at a 2 nm thickness. The Mg2Mo3O8 exhibits a relatively large remanent polarization ranging from 33 to 52 mu C cm(-)(2), which is tunable by changing its thickness. Notably, Mg2Mo3O8 possesses a high Curie temperature (>980 degrees C) across various thicknesses. Moreover, the as-grown Mg2Mo3O8 crystals display remarkable stability under harsh environments. This work introduces nolanites-type crystal into ultrathin ferroelectrics. The scalable synthesis of stable ultrathin ferroelectric Mg2Mo3O8 expands the scope of ferroelectric materials and may prosper applications of ferroelectrics.