Formation of Iron-Rich Phyllosilicates in the FeO–SiO2–H2O System During Hydrothermal Synthesis As a Function of Ph

The formation of iron-rich phyllosilicates can occur at different natural or engineered settings. In this study, the influence of pH in the hydrothermal synthesis of iron-rich phyllosilicates was investigated in the pH range 8.50-12.10 after the ageing of the precursor. The synthesized samples were characterized by powder X-ray diffraction, Raman and M & ouml;ssbauer spectroscopies and transmission electron microscopy. Three domains of pH were identified, and these correlated with silica availability and its speciation in the solution. The formation of 1:1-type FeIII/FeII phyllosilicate was observed between pH 9.67 and 10.75. Above pH 10.75, two types of phyllosilicate-like mineral phases were observed. In addition to 1:1-type FeIII/FeII phyllosilicate, 2:1-type FeIII/FeII phyllosilicate was observed. Below pH 9.67, mainly amorphous silica and iron oxides were observed. The findings show that pH governed the crystallinity and nature of the obtained phyllosilicate-like phases.