High-temperature Tribological Behaviour and Machining Performance of Self-Lubricant CrAlNAg Coatings for Dry Milling Operations
Tribology international(2024)
摘要
Tribological and machining performance of CrAlNAg coatings having different Ag content tested against AISI 1045 medium carbon steel were assessed. Wear track was evaluated by scanning electron microscopy and energy dispersive spectroscopy. 3D topography of wear track and ball counterpart was determined by non-contact type profilometer. The formation of different oxide phases on track was confirmed using Raman spectroscopy. CrAlNAg9 and CrAlNAg12 coatings were found beneficial in reducing material adhesion from counterpart thus providing protective layers to counterpart, whereas small addition of Ag did not provide any improvement on CrAlN coating performance. CrAlNAg9 coated milling inserts demonstrated best results in terms of reduction in chip temperature (~17.5%), cutting forces, surface roughness (~47%) and chip thickness (~12.7%) compared to uncoated inserts.
更多查看译文
关键词
CrAlNAg coatings,Tribology,Self-lubricating,High-temperature,Face milling,Tool wear
AI 理解论文
溯源树
样例
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要