Bio-Based Copolyester PEIFT: Enhanced Hydrophilicity, Rigidity, and Applications in Nanofibers

The raw materials of Poly(ethylene terephthalate) (PET) are derived from petroleum-based resources, which are no sustainable. Therefore, previous researchers introduced biomass-derived 2,5-tetrahydrofurfuryl dimethanol (THFDM) into PET. However, its heat resistance has decreased compared to PET. In this paper, a novel bio-based copolyester, poly(ethylene glycol-co-2,5-tetrahydrofuran dimethanol-co-isosorbide terephthalate) (PEIFT), is prepared by introducing biomass-derived isosorbide (ISB) and THFDM into the PET chains through melting copolymerization process. With the introduction of ISB content, copolyesters' hydrophilicity and rigidity improve. Compared to PET, glass transition temperature (Tg) increases by over 5 degrees C. In addition, the toughness and spinning performance of PEIFT have also been improved as a result of the addition of THFDM components. The hydrophobicity of PEIFTs electrospinning is greatly improved, with a contact angle exceeding 135 degrees. Finally, due to the good hydrophobicity of PEIFTs nanofibers, they have potential application value in the manufacture of hydrophobic nanofiber and filter films. Given its biomass source and excellent performance, they make it easier to replace materials derived from petroleum. Poly(ethylene glycol-co-2,5-tetrahydrofuran dimethanol-co-isosorbide terephthalate) (PEIFT), is prepared by introducing biomass-derived isosorbide (ISB) and 2,5-tetrahydrofurfuryl dimethanol (THFDM) into the PET chains through melting copolymerization process. PEIFTs nanofibers and films are prepared using electrospinning and solvent evaporation methods, respectively. It is found that PEIFTs have some advantages over PET due to introducing ISB and THFDM, such as better spinning performance and hydrophilicity. image