Tin-antimony/carbon composite porous fibers: electrospinning synthesis and application in sodium-ion batteries

In this work, tin-antimony/carbon composites porous fibers were successfully synthesized by an electrospinning method combined with two-step heat treatment processes, in which SnCl2 and SbCl3 were used as tin and antimony sources, and polyacrylonitrile (PAN) and polymethyl methacrylate (PMMA) were used as binders and pore-forming agents. The as-synthesized tin-antimony/carbon composites were systematically characterized by x-ray Diffraction (XRD), Transmission Electron Microscope (TEM), Scanning Electron Microscope (SEM), Energy-Dispersive Spectrometer (EDS), x-ray Photoelectron Spectroscopy (XPS), and Thermogravimetric Analysis-Differential Scanning Calorimetry (TG-DSC). The results indicate that the composite material consists of one-dimensional nitrogen-doped carbon porous fibers as the main matrix, with a three-dimensional network structure in which Sn, SnO2, and SnSb particles are encapsulated. Furthermore, the tin-antimony/carbon composites porous fibers were utilized as self-supported negative electrode for sodium-ion batteries. The results showed that the SNbM-2 sample electrode calcined at 800 degrees C demonstrated the best cycling stability and rate capability among all the sample electrodes, with a discharge capacity of 319.5 mAh center dot g-1 maintained after 100 cycles at a current density of 0.1 A center dot g-1. The excellent electrochemical performance of the SNbM-2 sample electrode is benefited from its unique porous structure and the carbon fiber network structure encapsulating Sn, SnO2, and SnSb particles, which could effectively shorten the Na+ ion transport distance and mitigate electrode volume expansion.