Influence of dual-cure resin-cement curing modes on gingival cytotoxicity and inflammatory responses

Background/purpose Dual-cure resin-cements are used for various dental restorations. However, whether the curing modes of these resin-cements influence gingival inflammation remains unclear. Hence, herein, we evaluated the effects of dual-cure resin-cement curing modes on gingival cytotoxicity and inflammatory responses. Materials and methods Specimens were prepared using two dual-cure resin-cements—RelyX Unicem 2 (RU) and G-CEM ONE (GO)—by light-cure or self-cure modes. Degree of conversion (DC) and monomer elution of the resin-cements were measured using Fourier-transform infrared spectroscopy and high-performance liquid chromatography, respectively. Human gingival fibroblasts (GFs) and macrophages were cultured on resin-cements, and inflammatory cytokine levels, intracellular reactive oxygen species (ROS) generation, and mitogen-activated protein (MAP) kinase activation were evaluated. Results Light-cured (LC) resin-cements exhibited significantly higher DC and lower monomer elution than did self-cured (SC) resin-cements. Triethyleneglycol dimethacrylate (TEGDMA) and urethane dimethacrylate (UDMA) were substantially eluted from RU and GO, respectively. Neither LC resin-cement exhibited cytotoxicity and enhanced pro-inflammatory cytokine expression in GFs and macrophages. However, both SC resin-cements significantly decreased cell numbers and promoted cellular inflammatory responses. SC generated higher intracellular ROS levels compared to that seen with LC, and different patterns of MAP kinase activation were observed between SC–RU and SC–GO. Conclusion Compared with LC dual-cure resin-cements, SC dual-cure resin-cements show stronger cytotoxicity and elicit greater inflammatory responses in gingival cells owing to residual monomers (e.g., TEGDMA and UDMA) by activating MAP kinases in GFs and macrophages. Clinicians should ensure adequate light irradiation during prosthesis cementation and make efforts to remove the excess cement.