High Energy-Storage Density and Giant Negative Electrocaloric Effect in PLZS Antiferroelectric Thick Film Ceramics Prepared Via the Tape-Casting Process
Journal of Alloys and Compounds(2024)
摘要
Antiferroelectric materials are highly desired for high energy-storage density capacitors and electrocaloric refrigerator in the future due to their excellent energy storage properties and giant negative electrocaloric effect, which have attracted great attention in recent years. In the present work, a highly recoverable energy density (Wrec) and a large reversible adiabatic temperature change (ΔT) were obtained simultaneously in PLZS thick film ceramics (TFCs). A maximum Wrec of 9.84J·cm-3 with an efficiency of 85.2% at 440kV·cm-1, and a negative ΔT of -9.50 °C at 280kV·cm-1 were obtained. Moreover, the maximum value of electrocaloric strength of 0.98K·m·MV-1 was achieved for Pb0.97La0.02(Zr0.50Sn0.50)O3 TFCs. These results demonstrate that the PLZS TFCs can be applied potentially for high energy-storage density capacitors and refrigerators.
更多查看译文
关键词
PLZS,antiferroelectric,energy storage performance,electrocaloric effect,electrocaloric strength
AI 理解论文
溯源树
样例
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要