XPS and NEXAFS Characterization of Mg/Zn and Mn Codoped Bismuth Tantalate Pyrochlores

Two series of the bismuth tantalate pyrochlore samples, codoped with Mg,Mn and Zn,Mn, were synthesized via solid-phase reaction. It was established that the Bi2Mg(Zn)(x)Mn1-xTa2O9.5-Delta (x = 0.3; 0.5; 0.7) samples contain the main phase of cubic pyrochlore (sp. gr. Fd-3m) and an admixture of triclinic BiTaO4 (sp. gr. P-1). In both sets, the amount of BiTaO4 is proportional to the amount of manganese doping, however, zinc-containing samples have a higher level of impurities than magnesium-containing ones. The unit cell parameter of the Zn,Mn codoped bismuth tantalate phase increases with an increasing content of zinc ions in the samples from 10.4895(5) (x = 0.3) to 10.5325(5) & Aring; (x = 0.7). The unit cell parameter of Mg,Mn codoped bismuth tantalate pyrochlores increases uniformly with an increasing index x(Mg) from 10.4970(8) at x = 0.3 to 10.5248(8) & Aring; at x = 0.7, according to the Vegard rule. The NEXAFS and XPS data showed that the ions were found to have oxidation states of Bi(+3), Ta(+5), Zn(+2) and Mg(+2). In the Ta 4f XPS spectrum of both series of samples, a low energy shift of the absorption band characteristic of tantalum ions with an effective charge of (+5-delta) was observed. The XPS spectra of Bi4f7/2 and Bi4f5/2 also show a shift of bands towards lower energies which is attributed to the presence of some low-charge ions of transition elements in the bismuth position. The NEXAFS spectroscopy data showed that manganese ions in both series of samples have predominantly 2+ and 3+ oxidation states. XPS data indicate that in zinc-containing preparations the proportion of oxidized manganese ions is higher than in magnesium-containing ones.