Revealing the Effect of Α’ Decomposition on Microstructure Evolution and Mechanical Properties in Ti80 Alloy

Three types of solution treatment and aging were designed to reveal the α’ decomposition and its effect on the mechanical properties of near-α Ti-80 alloy, as follows: solution at 970 °C then quenching (ST), ST + aging at 600 °C for 5 h (STA-1), and ST + aging 600 °C for 24 h (STA-2). The results show that the microstructures of the ST samples were mainly composed of equiaxed αp and acicular α’, with a large number of dislocations confirmed by the KAM results. After subsequent aging for 5 h, α’ decomposed into acicular fine αs and nano-β (intergranular β, intragranular β) in the STA-1 specimen, which obstructed dislocation motion during deformation, resulting in the STA-1 specimen exhibiting the most excellent yield strength (1012 MPa) and maintaining sufficient elongation (8.1%) compared with the ST (898 MPa) and STA-2 (871 MPa) samples. By further extending the aging time to 24 h, the size of acicular αs and nano-β gradually increased while the density of dislocations decreased, which resulted in a decrease in strength and an increase in plasticity. Based on this, a microstructures–properties correlation model was proposed. This study provides a new method for strength–plasticity matching of near-α titanium alloys through α’ decomposition to acicular αs+nano-β.