Irradiation induced hardening is commonly observed in structural materials, and is often associated with the degraded ductility. This study explores the role of thermomechanical processing (TMP) in mitigating irradiationinduced hardening in Incoloy 800H. The radiation response of solution-annealed and TMP-treated samples was systematically investigated to elucidate the underlying mechanisms of hardening reduction. Neutron irradiation was performed on solution-annealed and TMP-treated samples at 359, 431, and 580 degrees C, revealing consistently lower hardening in TMP samples. Microstructural characterization compared dislocation loops, cavities, clusters, and precipitates to assess their contributions to hardening. The strengthening contributions from individual microstructural features were estimated, and the microstructure-derived yield strength is consistent with the hardness-converted yield strength. The microstructure-properties correlation revealed the temperaturedependent primary hardening mechanism: dislocation loops dominated at lower temperature, whereas Ni3(Al, Ti) gamma ' precipitates were predominant at higher temperature. TMP reduced radiation-induced hardening through two mechanisms: (1) increased sink strength from dislocations and Ti(C,N) precipitates limited dislocation loop formation at lower temperatures, and (2) reduced Ti solute within the matrix in TMP samples suppressed gamma ' precipitate formation at higher temperatures. These findings identify the mechanisms governing radiationinduced hardening across different temperatures, which lays the foundation for TMP optimization for the development of advanced radiation-tolerant materials.

At high temperature conditions relevant to fossil and nuclear energy plants, Laves phase (Fe2X, X=Mo, W) precipitation is observed in common ferritic martensitic (FM) structural steels, with various reported effects on creep behavior. Despite being valuable metrics to correlate with mechanical properties and other precipitate phases, the volume fraction and number density of Laves phase precipitates has been difficult to quantify accurately using common techniques such as transmission electron microscopy (TEM) due to the relatively large size (similar to 0.25 mu m) and low number density (similar to 10(11) cm(-3)) of Laves precipitates. To address this characterization challenge, we developed and demonstrated a high-throughput and widely accessible method to quantify the volume fraction and number density of the Laves phase based on scanning electron microscope (SEM) images with a backscattered electron signal and the information depth (ID) of backscattered electrons. We applied this new technique in creep ruptured Grade 92 FM steel to study the effect of Laves phase on creep properties and determine the influence of stress on Laves phase precipitation. The quantitative accuracy of the SEM-based volume fraction and number density values was verified using synchrotron high energy X-ray diffraction and serial sectioning tomography. Stress did not significantly affect the Laves phase size or volume fraction during creep testing at 550 - 650 degrees C and stress levels of 90 - 260 MPa (vs. unstressed conditions). Conversely, a moderate but statistically significant stress-enhanced increase in Laves phase number density, corresponding to an increase in nucleation rate, occurred during creep exposure above 110 MPa.

Microstructural optimization to achieve greater mechanical strength has been one of the focuses in ferritic–martensitic steels development. However, these optimized microstructures’ effects on the radiation response are not well known. In this work, two ferritic–martensitic steels (9Cr-NbMo and 9Cr-Ta) underwent neutron irradiation in the High Flux Isotope Reactor, and their room-temperature post-irradiation tensile properties and microstructure evolutions were investigated and compared. These two steels exhibit similar pre-irradiation tensile behavior, and their yield strengths are higher than that of other ferritic–martensitic steels by about 200–250 MPa. Microstructural characterization on pre-irradiated materials reveals a smaller grain size in 9Cr-Ta (2.8 ± 0.3 μm in 9Cr-Ta versus 4.3 ± 0.5 μm in 9Cr-NbMo) but higher dislocation density and precipitate density in 9Cr-NbMo. As is common for ferritic–martensitic steels at low irradiation temperatures (less than about 0.45Tm), irradiation-induced hardening at 400 °C was observed for both alloys. Irradiation at 490 °C causes the two alloys to exhibit different tensile behavior: 9Cr-Ta softens by 208 MPa in yield stress, whereas 9Cr-NbMo maintains strength. Microstructural characterizations were performed, including precipitate growth, dislocation, and defect formation. Using the barrier hardening model for microstructure–property correlation, the softening in irradiated 9Cr-Ta is primarily attributed to the significant dislocation recovery, while the strength lost from the slight dislocation recovery in 9Cr-NbMo was compensated by the additional strength from the irradiation-induced cavities. The microstructure effect (primarily precipitate, dislocation and boundary) on the radiation response is discussed herein.

We describe our recent efforts demonstrating direct current sintering parameters appropriate to mimic near-identical microstructure to optimize reduced activation ferritic martensitic "castable nanostructured alloy". The fabrication process is presented, and through a combination of computational thermodynamics, multimodal characterization, and mechanical testing we confirm that sintering may be used to produce relevant castable nanostructured alloy (CNA). Our success in demonstrating the applicability of sintering to CNA fabrication opens the opportunity to fabricate functionally graded first wall tile structures or other complicated structures with demanding high-temperature performance, as example fusion high heat flux components.

Plasma-facing components (PFCs) are among the most critical gaps for fusion energy to establish technical and economic feasibility. Tungsten as a first wall/blanket material in PFCs requires to be integrating with reduced activation ferritic martensitic (RAFM) steels as a structural component. Currently, major drawbacks are the requirement of brazing, the formation of a brittle interface, and a large difference between the coefficients of thermal expansion of tungsten and steel. Here, a novel transitional multilayer structure was designed and investigated to join tungsten and RAFM steels using three interlayers. The composition of each interlayer was selected based on computational thermodynamics and diffusion kinetics to ensure a body-centered cubic (bcc) single-phase structure and prevent the formation of a brittle intermetallic phase region in the temperature range of 600-1150 & DEG;C. Although the transitional layer structure was designed for additive manufacturing, spark plasma sintering (SPS) as proof of concept was used to bond the individual layers. Interfaces were investigated using scanning and transmission electron microscopy methods but no layered intermetallic phase was observed. Nanoindentation maps across the interface suggest major hardness differences at the interface between tungsten and the vanadium interlayer, as well as the interface between RAFM steel and the FeCrAl interlayer.& COPY; 2023 The Authors. Published by Elsevier B.V. This is an open access article under the CC BY-NC-ND license (http://creativecommons.org/licenses/by-nc-nd/4.0/).

The main focus of data augmentation research has been on the enhancement of generation models, leaving the examination and improvements of synthetic data evaluation methods less explored.In our work, we explore a number of sentence similarity measures in the context of data generation filtering, and evaluate their impact on the performance of the targeted Natural Language Understanding problem for the example of intent classification and named entity recognition tasks.Our experiments on ATIS dataset show that the right choice of filtering technique can bring up to 33% in sentence accuracy improvement for targeted underrepresented intents.

As a candidate material for advanced nuclear reactors, a ferritic-martensitic (FM) steel Grade 92 in the standard normalized and tempered (NT) condition was subjected to two types of thermomechanical treatments (TMTs) with one having a lower level of deformation (T5A) and the other having a higher level of deformation (T5B). The testing results of the three conditions indicated that the TMTs significantly improved yield strength, creep resistance, fracture toughness, and sodium corrosion resistance compared with the NT condition. T5A excelled at creep resistance while T5B at sodium corrosion resistance. Microstructural characterization of the three conditions supports the varied enhancements in the properties. This study suggests that an appropriate TMT can be developed and applied to FM steels to better meet specific application requirements.

Limited studies have evaluated the creep behavior of additively manufactured (AM) ferritic-martensitic (FM) steels. This work investigated the creep behavior of a 9Cr FM steel fabricated by powder blown directed energy deposition (DED) technique. The creep testing at 550-650 degrees C and 150 MPa for the spec-imens along the deposition direction in the as-built condition, together with corresponding microstruc-tural characterization, revealed a threshold temperature between 600 and 625 degrees C, below which the steel has creep resistance comparable with Grade 91 cross-welds and noticeably greater than 9Cr-1Mo steel. The threshold temperature distinguishes the creep behavior in two regimes differentiated in creep ac-tivation energy, creep deformation, and failure mechanism. Unlike the creep rupture surface similar to 45 degrees from the loading direction when tested above the threshold temperature, the creep rupture for testing below the threshold temperature resembles type IV failure in the cross-welds of ferritic steels. The DED-induced layer structure in the as-built steel played a significant role on the change of creep behavior. (c) 2022 Elsevier B.V. All rights reserved.

Characterization methods capable of providing critical information across multiple structural length scales are essential in materials exposed to the extreme environments such as anticipated fusion power systems. Complementary techniques capable of uncovering the complicated microstructural irradiation-induced evolution are also important to verify and validate advanced computational models. To date, the primary microstructural tools informing such lower-length scale models have included analytical electron microscopy, positron annihilation spectroscopy, atom probe tomography, and small-angle neutron scattering. In this paper, we discuss the application of state-of-the-art synchrotron-based x-ray characterization methods in fusion material research. Specifically highlighted are opportunities in leveraging synchrotron-based techniques to address fundamental and applied materials science challenges at various length scales and in support of modeling efforts. Examples presented in this article include: a combined small angle x-ray scattering and x-ray diffraction study of transmutation-induced precipitation in neutron irradiated tungsten, and the identification of size and structure of nm-scale transmutation precipitates and voids; quantitative characterization of thermodynamically predicted minor precipitate populations in advanced reduced activation ferritic-martensitic steels through high energy x-ray diffraction; and a review of recent synchrotron-based studies dedicated to quantifying the radiation response of fusion relevant materials. The latter includes a pair distribution function analysis investigation of neutron irradiated SiC with insights into the different radiation response of the silicon and carbon sublattices, and a dose dependent decrease in the size of defect free material.

NF616 is a third-generation ferritic martensitic steel, developed to have better creep resistance than the prior generation T91. Unlike relatively numerous studies of T91, there is a lack of understanding of the irradiation effect on the microstructural evolution and mechanical response of NF616. This work evaluated the microstructures and radiation hardening of NF616 irradiated up to 8.2 displacement per atom (dpa) at 292 degrees C-431 degrees C, compared with T91 from two heats. Dislocation loops were observed in all investigated samples. NF616 exhibited comparable loop size but slightly lower loop density than those in the general T91 heat at 430 degrees C. Cavities were only observed in NF616 at 431 degrees C but absent at lower irradiation temperatures (292 degrees C and 359 degrees C). Ni-rich clusters were also observed in NF616 at 431 degrees C, while only weak Ni-clustering were observed at lower irradiation temperatures. Compared to the general T91 heat, NF616 demonstrated better swelling resistance (e.g., one third of swelling in the general T91 heat at 430 degrees C), a slightly higher number density of Ni-rich clusters, and slightly lower radiation hardening. The low-carbon T91 showed the greatest hardening with the largest swelling and loop sizes, despite its lowest irradiation temperature and intermediate dose. The calculated hardening from loops, cavities and Ni-rich clusters using the classic dispersed barrier-hardening model had reasonable agreement with the experiment-derived results, with the primary hardening contribution attributed to dislocation loops. (c) 2021 Elsevier B.V. All rights reserved.

Detailed investigations of two ferritic-martensitic steels, i.e., Nb- and Ta-steel, indicate that the higher Nb diffusivity and the lower nucleation driving force of Nb-carbide promote preferential nucleation of Nb-carbides at grain boundaries and thus a higher boundary occupancy than Ta-carbides, which favored greater creep resistance of Nb-steel than that of Ta-steel despite their similar yield strength.

Substantial residual tensile stress tends to accumulate in currently available high-Cr ferritic martensitic steels that are subjected to cyclical heat treatment, which leads to premature brittle fracture. By tailoring the alloy composition, this thermal cycling can be exploited to induce a high number density of nanoprecipitates and phase transformations countering residual tensile stresses. In this work, three new variants of ferritic-martensitic steels have been designed with computational thermodynamics to meet the goals of mitigating residual tensile stresses by lowering martensite start temperatures and of enhancing mechanical strength and irradiation sink strength by increasing the number density of nanoprecipitates. Cast materials were subjected to cyclical heat treatment. The thermally cycled samples were evaluated with mechanical testing and microstructural analysis to identify the optimal composition in which figures of merit include low residual stress and a high density of nanoscale MX (M = metal, X = C/N) precipitates, leading to high yield strength with reasonable ductility. The noticeably higher density of nanoprecipitates in the optimal alloy favor its higher yield strength, which is supported by the microstructure-derived yield strength calculation and precipitation kinetics simulation.

Understanding the effects of helium on microstructures and mechanical properties of reduced-activation ferritic-martensitic steels is important to use of these steels in fusion reactor structures. The 9Cr-2WVTa steels were doped with 58Ni and 60Ni isotopes at 2 weight percent to control the rate of transmutation helium generation. The samples were irradiated in the High Flux Isotope Reactor to ~24 displacements per atom at nominal temperatures of 300, 400, and 500°C, producing 228 and 7 atomic parts-per-million helium in the 58Ni- and 60Ni-doped samples, respectively. Transmission electron microscopy revealed a variety of precipitates and the radiation-induced dislocation loops and cavities (voids or helium bubbles). Tensile tests of the irradiated samples at the irradiation temperatures showed radiation-induced hardening at 300°C and radiation-induced softening at 400°C. Analysis indicates that the hardening primarily originated from the loops and cavities. The 58Ni-doped samples had greater strengthening contributions from loops and cavities, leading to higher hardening with lower ductility than the 60Ni-doped samples. The greater helium production of 58Ni did not show pronounced reductions in ductility of the samples.

A reduced activation ferritic/martensitic steel, Eurofer97, was neutron irradiated in the vicinity of 300 degrees C in the High Flux Isotope Reactor (HFIR) up to 72 dpa. Advanced analytical scanning transmission electron microscopy and conventional transmission electron microscopy were applied to investigate the radiation-induced segregation and phase instability behavior after neutron irradiation. Amorphization was observed in M23C6 carbides. Cr-rich clusters were seen within the matrix, near the lath boundaries and close to the M23C6 carbides. Cr enrichment and Fe depletion were detected at both prior austenite grain boundaries and lath boundaries, despite different segregation magnitude. In addition, the enrichment of Ni, the depletion of V, and tiny cavities (presumably helium bubbles) are also found at lath boundaries. This work interrogates the evolution of microstructures after neutron irradiation, which provides detailed understanding on the microstructural aspects controlling the mechanical integrity of Eurofer97 under high-dose neutron damage. (C) 2021 Elsevier B.V. All rights reserved.

Helium bubble formation was examined by scanning/transmission electron microscopy (S/TEM) in Fe-9/10Cr binary alloys and two dispersion strengthened nanostructured alloys (CNA3 and 14YWT containing 5-10 nm diameter carbide and oxide particles, respectively) after ex-situ and in-situ He implantation to similar to 10,000 appm at 500 to 900 degrees C. The combination of high-resolution STEM images and electron energy loss spectroscopy (EELS) revealed that the Y-Ti-O nanoparticles in 14YWT were uniformly distributed and exhibited a one-to-one relationship for bubble attachment to the nanoclusters. In the in-situ experiment at 900 degrees C, grain boundary cracking was severe in the Fe-10Cr model alloy, but not in the nanostructured alloys. From 500 to 900 degrees C, the bubble size generally increased with increasing irradiation temperature, while the bubble density decreased with increasing temperature. At the same temperatures, the bubble size in the implanted materials was in the order of Fe-9/10Cr > CNA3 > 14YWT, while the bubble density showed the opposite order. The observed bubble number densities for the nanostructured alloys are comparable to the nanoparticle density, suggesting that the nanoparticles in both alloys were effective in trapping He. Our results indicate that very high He concentrations can be managed in nanostructured alloys by sequestering the helium into smaller bubbles (which leads to a lower volume swelling value) and to shield He from the grain boundaries. This can be attributed to the much higher sink strength associated with the nanoclusters or the He trapping ability between different types of nanoclusters. (C) 2021 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Life extension of the existing nuclear reactors imposes accumulated damages, such as higher fluences and longer periods of corrosion, to structural materials, which would result in significant challenges to the traditional reactor materials such as type 304 and 316 stainless steels. Advanced alloys with superior radiation resistance will increase safety margins, design flexibility, and economics for not only the life extension of the existing fleet but also new builds with advanced reactor designs. The Electric Power Research Institute (EPRI) initiated a collaboration with the Department of Energy (DOE) Light Water Reactor Sustainability (LWRS) Program on the Advanced Radiation Resistant Materials (ARRM) program, focused on developing and test degradation resistant alloys for light water reactor (LWR)- relevant environments. Based on a comprehensive microstructure and property screening, the ARRM program selected a total of five alloys (i.e., Grade 92, 310, 690, 718A, and 725), together with 316L and X-750 as references, for further investigations.

A newly developed nano-structured high-Mn 9Cr ferritic-martensitic (FM) steel designed for additive manufacturing (Additive-manufactured Nanostructured Alloy, ANA) was fabricated via the direct energy deposition method. The as-printed ANA2 showed tensile properties (strength and elongation) and Charpy impact toughness (upper-shelf energy and ductile-brittle transition temperature) comparable to oxide-dispersion-strengthened (ODS) Eurofer and PM2000. Compared with wrought P91, the as-built ANA2 showed significantly higher yield strength but inferior Charpy impact toughness and ductility. Microstructural characterization revealed uniformly distributed sub-micron pores, an extremely high dislocation density, and a high density of ultrafine nano-structured precipitates in the matrix. The microstructures indicated the dislocations as the dominant strengthening element and the ultrafine precipitates as the primary contribution to estimated irradiation sink density. This work demonstrates the ability to exploit the unique consolidation properties of additive manufacturing to fabricate steels which marry the benefits of both ODS alloys and conventionally processed FM steels.

Single-phase high- and medium-entropy alloys with face-centred cubic (fcc) structure can exhibit high tensile ductility1,2 and excellent toughness2,3, but their room-temperature strengths are low1–3. Dislocation obstacles such as grain boundaries4, twin boundaries5, solute atoms6 and precipitates7–9 can increase strength. However, with few exceptions8–11, such obstacles tend to decrease ductility. Interestingly, precipitates can also hinder phase transformations12,13. Here, using a model, precipitate-strengthened, Fe–Ni–Al–Ti medium-entropy alloy, we demonstrate a strategy that combines these dual functions in a single alloy. The nanoprecipitates in our alloy, in addition to providing conventional strengthening of the matrix, also modulate its transformation from fcc-austenite to body-centred cubic (bcc) martensite, constraining it to remain as metastable fcc after quenching through the transformation temperature. During subsequent tensile testing, the matrix progressively transforms to bcc-martensite, enabling substantial increases in strength, work hardening and ductility. This use of nanoprecipitates exploits synergies between precipitation strengthening and transformation-induced plasticity, resulting in simultaneous enhancement of tensile strength and uniform elongation. Our findings demonstrate how synergistic deformation mechanisms can be deliberately activated, exactly when needed, by altering precipitate characteristics (such as size, spacing, and so on), along with the chemical driving force for phase transformation, to optimize strength and ductility. Increased strength and ductility in a medium-entropy alloy of Fe, Ni, Al and Ti is demonstrated using nanoprecipitates that simultaneously hinder phase transformation and block dislocation motion.

Ferritic-martensitic steels G92-2b (an optimized Grade 92 heat), NF616 and T91, and austenitic stainless steel 800H and its Grain Boundary Engineering (GBE)-treated version 800H-TMP (ThermoMechanical Processing) were irradiated in the High Flux Isotope Reactor (HFIR) of Oak Ridge National Laboratory (ORNL) and the Advanced Test Reactor (ATR) of Idaho National Laboratory (INL). Selected G92-2b samples were irradiated up to 14.66 dpa in the HFIR at two temperature ranges: 400–496.7°C and 683.3– 720°C. NF616 and T91 were irradiated in the ATR up to 8.16 dpa with the irradiation temperatures ranged from 241°C to 447.5°C. Alloy 800H and 800H-TMP samples were irradiated in both the HFIR and the ATR. Selected 800H and 800H-TMP samples had HFIR irradiation to 1.28 dpa at 580°C and ATR irradiation up to 9.12 dpa at 359°C to 431°C. Vickers hardness measurements, fractography, and microstructural characterization were performed on the selected samples in the Low Activation Materials Design and Analysis (LAMDA) laboratory. Radiation-hardening of G92-2b was observed at the lower doses and lower irradiation temperatures (400- 496.7°C), with GB03 (0.52 dpa at 400°C) and GB04 (7.44 dpa at ~490°C) showing ~12% and ~8% hardening, respectively. Softening by ~14% was observed for GB05 (14.66 dpa at 496.7°C). Radiationsoftening of G92-2b was more prevalent at the higher irradiation temperatures (683.3-~720°C), with GB10 (0.46 dpa at 683.3°C), GB11 (7.44 dpa at ~720°C), and GB12 (14.63 dpa at ~720°C) showing ~8%, ~8%, and ~40% softening, respectively. Radiation-hardening of NF616 and T91 was observed with the hardness increased by ~37% to ~65% depending on the irradiation doses and irradiation temperatures. Within the studied irradiation conditions of NF616 and T91, samples with a higher dose had a larger hardness after irradiation. All the tested alloy 800H and 800H-TMP samples in this work showed radiation-hardening by ~96±7% to ~152±10%. Alloy 800H-TMP tended to have slightly smaller radiation-hardening than alloy 800H. The fractography results of G92-2b sample GB03, GB10, and GB11, together with the previously characterized fractography of GB04, GB05, and GB12, indicated that the ductility of G92-2b was maintained up to 14.66 dpa at the lower irradiation temperatures of 400-496.7°C, while some loss of ductility (less necking) was observed for higher doses at the higher irradiation temperatures of 683.3-720°C. This agrees with the previously reported tensile test results of G92-2b, where the elongation of G92-2b was reduced at higher doses at the higher irradiation temperatures. Dimple sizes increased at higher doses, which are more evident at the higher irradiation temperatures of 683.3-~720°C. The fractography of NF616 sample D2 (2.96 dpa at 291.5°C), D4 (5.91 dpa at 359°C), and D6 (8.16 dpa at 431°C) indicated loss of ductility with negligible necking for sample D2, while ductile failure for samples D4 and D6. Fractography of alloy 800H and 800H-TMP samples in various irradiation conditions showed ductile failure with obvious necking. Dimples were observed, with some of them containing large Ti-rich particles, in all the 800H/800H-TMP samples. Electron backscatter diffraction characterization of GB12 indicated the recovery of the lath structure, which was generally replaced by an equiaxed grain structure. Transmission electron microscopy (TEM) characterization showed the presence of frequent M23C6 (M = primarily Cr), MX (M = primarily V), spherical Nb(C,N) precipitates, and occasional Laves phase precipitates in the G92-2b samples. MX precipitates with sizes of 20-30 nm were observed at boundaries of smaller grains, indicating the pinning effect of the V-rich precipitates. The lath structure recovery was more evident at the higher irradiation temperatures (683.3-~720°C), with decreased densities of line dislocations and M23C6 precipitates. The irradiated T91 (TA04) showed the growth of M23C6 precipitates to 101 ± 40 nm from the initial 68 ± 22 nm in the unirradiated condition. Dislocation loops of both {100} and {111} types were present in TA04. TEM characterization was also performed on the irradiated 800H (N4, N5, N6, and AR2) and 800H-TMP (P4, P5, P6, and HG1). Accumulation of M23C6 precipitates at grain boundaries was observed in all the xii 800H/800H-TMP samples, and the presence of Ti(C,N) precipitates at grain boundaries and in the matrix was observed in the irradiated 800H-TMP. Some Ti(C,N) precipitates are embedded in the M23C6 precipitates, maintaining specific orientation relationships between the precipitates and between the precipitate and matrix. In addition, nanoscale Si-rich clusters were observed in the matrix of all the 800H/800H-TMP samples, with EDS Si maps tending to have a lower contrast in 800H-TMP samples. Atom probe tomography was conducted on the same samples, supported by a Rapid Turnaround Examination project under Nuclear Science User Facilities. The results are being analyzed to be integrated with the TEM results for a confident description of the γ’ precipitates. Dislocation loops also formed in all the 800H/800H-TMP samples. The density and the average size of dislocation loops were quantified to be in the order of 1022 – 1023 m-3 and 11.7 – 15.9 nm, respectively, in the ATR-irradiated 800H/800H-TMP samples. The loop densities in irradiated 800H were higher than that in irradiated 800H-TMP under the same irradiation conditions. Further systematic data analyses, together with some complementary experiments, will be pursued for these samples to foster peer-reviewed journal article publications.