The reaction of epoxyphosphazenes with methacrylic acid was used to synthesize methacrylate-containing phosphazene oligomers (MPO) used to modify dental restorative materials.The introduction of 1015 wt.% MPO into the base bis-methacrylate binder composition can significantly increase the adhesion of modified cured compositions to tooth tissues and metals, as well as improve water resistance while maintaining the required strength indicators and other physicochemical characteristics required by GOST.

The aryloxyphosphazenes containing carboxylic groups in phosphorus-linked radicals and capable of copolymerization with acrylic binders were used as modifiers of dental polymer compositions. Filled modified dental compositions have been obtained and tested. It has been shown that the best mechanical and physicochemical parameters are exhibited by cured compositions with a modifier based on aryloxyphosphazene with 4-hydroxycinnamic and eugenol radicals in the phosphazene ring.

Цели и задачи: клиническая оценка проведена с целью проверки клинической эффективности и безопасности остеопластического материала Биопласт-Дент (ВладМиВа). Материалы и методы. Анализ и оценка клинических данных литературы о медицинском изделии — материале Биопласт-Дент. Результаты. Результаты изученных нами публикаций российских и зарубежных научных изданий, отражающих результаты клинических и лабораторных исследований, свидетельствуют о биосовместимости Биопласт-Дента и эффективности его применения для замещения костных дефектов вследствие ускорения процессов регенерации костной ткани. Данный материал по микроструктуре, химическому составу и скорости биорезорбции близок к кости человека, положительно влияет на процессы ее перестройки и восстановления. В клинических исследованиях показана успешность использования Биопласт-Дента при хирургическом лечении переломов нижней челюсти, ретинированных зубов и кист челюстей. Клинически обоснована эффективность применения Биопласт-Дента при лечении пациентов с хроническим генерализованным пародонтитом и непосредственной дентальной имплантации. Его совместное применение с резорбируемой мембраной Биопласт-Дент облегчает течение и сокращает срок реабилитационного периода, снижает риск возникновения осложнений. Гель Биопласт-Дент оказывает благоприятное влияние на динамику хронического воспалительного процесса тканей пародонта. Заключение. На основании изученных нами данных литературы установлена клиническая эффективность и безопасность материала Биопласт-Дент, применяемого для замещения костных дефектов в клинике стоматологии и челюстно-лицевой хирургии.

Methacrylate-containing silsesquioxane–siloxane oligomers with M w = (2–20) × 10 3 determined by gel permeation chromatography (GPC) are synthesized by acidohydrolytic copolycondensation of γ‑methacryloxypropyltrimethoxysilane and diorganodialkoxysilanes. According to the data of 29 Si NMR spectro-scopy, the molecules of these oligomers contain silsesquioxane units (RSiO 1.5 ) n , where R is a γ-methacryloxypropyl radical, and mixed cyclic structures of the (RSiO 1.5 ) m (R'R''SiO) p type, where R' is CH 3 and R'' is CH 3 or C 6 H 5 , with linear diorganosiloxane fragments added to them. The introduction of 6 wt % silsesquioxane–siloxane oligomers into a filled base dental compound based on a mixture of bismethacrylates increases its mechanical characteristics by more than a factor of 1.25–1.75 with a simultaneous substantial decrease in the polymerization shrinkage, water uptake, and water solubility.

Methacrylate-containing oligosilsesquioxanes were synthesized by acidohydrolytic copolycondensation of γ-methacryloyloxypropyltrimethoxysilane and phenyltrimethoxysilane in a mixture of bismethacrylate monomers, 2,2-bis[4-(2-hydroxy-3-methacryloyloxypropyl)phenyl]propane and triethylene glycol dimethacrylate, and were characterized by NMR spectroscopy and MALDI-TOF mass spectrometry. Performing the process in the bismethacrylate medium favors formation of uniform blends. Their introduction in an amount of 3 wt % into filled methacrylate dental composites considerably improves the physicomechanical characteristics of these composites.

Triethoxysilylphosphazenes have been synthesized via hydrosilylation of cyclotriphosphazenes with various contents of 4-allyl-2-methoxyphenoxy groups by triethoxysilane at an equimolar phosphazene–silane ratio. Hydrolytic copolycondensation of the latter compounds with ?-methacryloxypropyltrimethoxysilane resulted in oligosiloxanes involving functional methacrylic and phosphazene fragments. The oligomers have been used as additives to a dental composition based on bisphenol A-diglycidyl methacrylate and triethylene glycol dimethacrylate. The modified filled compositions are characterized by reduced (4-fold) sensitivity to external illumination and improved strength properties and microhardness.

Methyl acrylate oligosilsesquioxanes based on γ-methacryloxypropyltrimethoxysilane and its mixtures with phenyltrimethoxysilane have been synthesized through acidohydrolytic polycondensation and studied via NMR spectroscopy and MALDI-TOF mass spectrometry. It is shown that the addition of the aforementioned oligosilsesquioxanes to a dental composition based on 2,2-bis[ p -(3-metacryloyloxy-2-hydroxypropoxy)phenyl]propane and triethylene glycol dimethacrylate improves the mechanical characteristics of cured polymer composites.

Методом ацидогидролитической поликонденсации синтезированы и с помощью ЯМР-спектроскопии и масс-спектрометрии MALDI-TOF исследованы метакрилатсодержащие олигосилсесквиоксаны на основе -метакрилоксипропилтриметоксисилана и его смесей с фенилтриметоксисиланом. Добавки указанных олигосилсесквиоксанов в стоматологическую композицию на основе 2,2-бис-[n-(3-метакрилоилокси-2-гидроксипропокси)фенил]пропана и диметакрилата триэтиленгликоля улучшают физико-механические характеристики отвержденного полимерного композита.

Methacrylate-containing organosilsesquioxanes with M n = (1.5−5.0) × 10 3 were synthesized via hydrolytic polycondensation of γ-methacryloxypropyltrimethoxysilane under different conditions. On the basis of comparison of 29 Si NMR data and the molecular masses of the oligomers, it was concluded that oligomer molecules contain 8–12-membered siloxane cycles.