压力管道属于有较大危害性的特种设备，具有应用领域广、跨越空间大、承载压力大、输送介质多等特点。裂纹是压力管道最容易产生同时也是最具危害性的缺陷，裂纹扩展到一定程度可造成材料断裂，从而导致安全事故的发生。本文介绍压力管道焊接裂纹、疲劳裂纹和应力腐蚀裂纹等几种常见的几种裂纹产生的机理，然后提出原材料质量控制、原材料生产质量控制和焊接工艺的控制等预防裂纹产生的若干措施，最后介绍压力管道检验裂纹的内容与方法。

In this paper, it carried out the mechanical properties test, microstructure observation and SEM scan test for the welded joint of automatic submerged arc welding about X90M pipeline steel plate. The tests showed that the weld microstructure is mainly composed of acicular ferrite and granular bainite,the heat affected zone(HAZ) includes granular bainite and a small amount of blocky ferrite. The hardness test results showed that no obvious softening phenomenon exist in HAZ, the impact absorbed energy of the weld and HAZ are more sensitive to temperature, but the cross distribution of acicular ferrite in the weld and the columnar crystal state leads to the toughness is a bit poor to HAZ. The impact fracture appearance of the base metal and HAZ below 0℃display the dimple shape, and the weld fracture morphology is quasi cleavage feature.

采用多种焊材组合并配合不同焊接线能量对X90M钢板进行工艺评定,并通过有关测试分析.所选择的焊材、工艺参数等均满足要求.为提高接头强度和低温韧性等性能,在满足外观成型的前提下,应尽量采用较低的焊接线能量.

近年来随着氨制冷的普遍发展，氨制冷管道也频繁出现各种事故。通过两起典型的液氨管道泄露事故，分析了氨制冷压力管道方面存在的一些问题，并提出了一些检验重点。

系统介绍了长输管道焊接过程中裂纹产生的原因和分类,以及控制裂纹产生的若干措施。

系统介绍了燃气用PE管的焊接工艺、热熔焊的质量控制要点和监检过程中的主要注意事项.燃气用PE管大多采用热熔对接连接,分别阐述了温度、压力、时间、接头质量等影响其质量的主要因素,并从施工验收规范、材料验收、焊接及焊接检验、管道敷设、试验与验收等方面介绍了燃气用聚乙烯PE管道安装监督检验应注意的问题.