Using the method of impedance spectroscopy and optical density measurements, the diffusion of oxygen in single crystals of lithium niobate of the congruent composition after the reductive thermochemical processing is studied. The parameters describing the diffusion of oxygen in the temperature range 493–693 K are established.

AbstractUsing the method of impedance spectroscopy and optical density measurements, the diffusion of oxygen in single crystals of lithium niobate of the congruent composition after the reductive thermochemical processing is studied. The parameters describing the diffusion of oxygen in the temperature range 493–693 K are established.

The instability of the electrical properties of lithium niobate single crystals of congruent composition subjected to reducing thermochemical treatment has been investigated by impedance spectroscopy. It has been shown that the subsequent heating of the reduced lithium niobate samples in dry air up to 380 K or higher is accompanied by the progressive increase in their electric resistance, which is due to the oxidization of the crystal surface layers.