Rhombus-shaped microobjects formed by strips of two micrometers wide were fabricated from the spin valve film. The influence of the shape anisotropy on the layers magnetic moment rotation during the spin valve magnetic reversal is studied. A method for two-stage thermomagnetic treatment in a direction-fixed magnetic field has been found. The method allows to obtain the opposite sign values of the exchange bias fields in the non-parallel rhombus sides. The direction of the formed exchange bias is determined by the deviation of the strip from the uniaxial anisotropy axis and from the magnetic field applied during thermomagnetic treatment. Based on a rhombus-shaped microobject made from a single spin valve film, the device is a Full Wheatstone bridge. Each side of the rhombus is an active magnetically sensitive element.

The microwave giant magnetoresistance effect in a (CoFe/Cu) superlattice with micron-sized holes has been studied. Measurements of the frequency dependences of the transmission coefficient, as well as the dependences of the microwave transmission and reflection coefficients on the magnetic field, are performed. The measurements were performed on the superlattice samples without holes, having one hole with a diameter of 6.3 m and seven holes with a diameter of 1.7 m. It is shown that the presence of a hole with a diameter of 6.3 m leads to a significant frequency dependence of the microwave giant magnetoresistance effect. Magnetic and magnetoresistance measurements of superlattice samples were performed.

Получен магнитный сорбент на основе терморасширенного графита, модифицированного ферритом магния, путем пропитки окисленного графита в смешанном растворе FeCl3 и Mg(NO3)2 с последующей термообработкой пропитанного окисленного графита на воздухе. Методами рентгенофазового анализа и мессбауэровской спектроскопии показано, что структура феррита магния представляет собой обращенную шпинель со степенью инверсии 0.59. Намагниченность насыщения полученного терморасширенного графита, содержащего феррит магния, составляла 16.1 эме/г, в то время как его сорбционная емкость по отношению к нефти достигала 54 г/г. При прессовании терморасширенного графита до плотности 0.03 г/см3 его сорбционная емкость уменьшалась до 26 г/г, дальнейшее увеличение плотности приводило к значительному снижению сорбционной способности образца.