It is shown that single-mode fluorosilicate optical fibers fabricated with the aid of modified chemical vapor deposition exhibit a significant decrease in the radiation resistance when 1 mol % GeO 2 is introduced into the silica-glass core. Elimination of chlorine and OH group impurities in the silica glass of the core of the fluorosilicate single-mode fiber leads to a relatively low level of radiation-induced attenuation. Prior to radiation processing, the loss factors of optical fiber are 0.18 and 0.3 dB/km at wavelengths of 1.55 and 1.31 μm, respectively. The dependence of optical loss of such fibers on the bend diameter ranging from 6 to 12 mm is studied.

Установлено, что одномодовые фторсиликатные волоконные световоды, изготавливаемые модифицированным методом химического парофазного осаждения, резко снижают радиационную стойкость при введении в сердцевину из кварцевого стекла 1 mol.% GeO2. Устранением примесей хлора и OH-групп из кварцевого стекла сердцевины фторсиликатного одномодового волоконного световода достигнут низкий уровень радиационно-наведенных оптических потерь. Затухание волоконного световода до радиационной обработки равно 0.18 и 0.3 dB/km на длине волны 1.55 и 1.31 μm соответственно. Исследована зависимость оптических потерь таких световодов от диаметра их изгиба в диапазоне 6-12 mm. Ключевые слова: MCVD-метод, одномодовые световоды, фторсиликатная оболочка, оптические потери, радиационная стойкость.

The surface relief of blanks and silica glass fibers is studied by atomic force microscopy. The temperature change during free cooling is recorded using an infrared pyrometer. The results of the measurements of the roughness of the blank and fiber could indicate the effect of the cooling time of the quartz glass (QG) on the morphology of its surface.

The causes of the occurrence and the method of the elimination of defects of non-bridging oxygen in multimode fluorosilicate optical fibers prepared by the modified method of chemical vapor deposition are considered. The solution is the use of support tubes obtained by quartz surfacing in a hydrogen atmosphere. In this case, there is no absorption band in a range of 630 nm caused by nonbridging oxygen in the spectrum of optical losses of gradient fluorosilicate optical fibers of W-type. Attenuation in a visible spectrum range is mainly determined by the level of Rayleigh scattering and the mode dispersions at a wavelength of 342 and 683 nm are 1.2 ± 0.1 and 0.7 ± 0.2 ps/m, respectively.

© К.В. Дукельский , Г.М. Ермолаева , М.А. Ероньян , А.В. Комаров , А.А. Реуцкий , В.Б. Шилов , А.А. Щеглов 3 1 Санкт-Петербургский государственный университет телекоммуникаций им. проф. М.А. Бонч-Бруевича, 193232 Санкт-Петербург, Россия 2 Государственный оптический институт им. С.И. Вавилова, 199034 Санкт-Петербург, Россия 3 Концерн ” Центральный научно-исследовательский институт ” Электроприбор“, 197046 Санкт-Петербург, Россия 4 НПО Научно-исследовательский и технологический институт оптического материаловедения Государственного оптического института им. С.И. Вавилова, 192171 Санкт-Петербург, Россия 5 Университет ИТМО, 197101 Санкт-Петербург, Россия

In this paper, we discuss how the drawing temperature of quartz light guides with germanosilicate cores and outer borosilicate cladding affects their strength and optical losses. The low-viscosity cladding of a light guide allows the drawing temperature to be decreased to 1950 degrees C, which, in turn, leads to increased strength and helps reduce excessive optical losses. (C) 2017 Optical Society of America