Acetaminophen (APAP) is a well-known type of over-the-counter painkillers and is frequently found in surface waterbodies, causing hepatotoxicity and skin irritation. Due to its persistence and chronic effects on the environment, innovative solutions must be provided to decompose APAP, effectively. Innovative catalysts of tungsten-modified iron oxides (TF) were successfully developed via a combustion method and thoroughly characterized using SEM, TEM, XRD, XPS, a porosimetry analysis, Mössbauer spectroscopy, VSM magnetometry, and EPR. With the synthesis method, tungsten was successfully incorporated into iron oxides to form ferrites and other magnetic iron oxides with a high porosity of 19.7 % and a large surface area of 29.5 m2/g. Also, their catalytic activities for APAP degradation by activating peroxymonosulfate (PMS) were evaluated under various conditions. Under optimal conditions, TF 2.0 showed the highest APAP degradation of 95 % removal with a catalyst loading of 2.0 g/L, initial APAP concentration of 5 mg/L, PMS of 6.5 mM, and pH 2.15 at room temperature. No inhibition by solution pHs, alkalinity, and humic acid was observed for APAP degradation in this study. The catalysts also showed chemical and mechanical stability, achieving 100 % degradation of 1 mg/L APAP during reusability tests with three consecutive experiments. These results show that TFs can effectively degrade persistent contaminants of emerging concern in water, offering an impactful contribution to wastewater treatment to protect human health and the ecosystem.

This paper reviews the currently used pretreatment methods for microplastics (MPs) analysis in soil and freshwater sediments, primarily sample processing, pretreatment, and characterization methods for MPs analysis. In addition, analytical tools (e.g., lab instruments), MPs characteristics, and MPs quantity, are included in this review. Prior to pretreatment, soil and sediment samples are typically processed using sieving and drying methods, and a sample quantity of <50 g was mostly used for the pretreatment. Density separation was commonly performed before organic matter removal. Sodium chloride (NaCl) and zinc chloride (ZnCl2) were most often used for density separation, and hydrogen peroxide (H2O2) oxidation was most frequently used to remove organic matter. Although advantages of each pretreatment method have been investigated, it is still challenging to determine a universal pretreatment method due to sample variability (e.g., sample characteristics). Furthermore, it is highly required to establish standard pretreatment methods that can be used for various environmental matrices, including air, water, and wastes as well as soil and sediment.

Galvanic replacement reaction was used in the synthesis of bimetallic gold–silver alloy nanoparticles (Au–Ag NPs), where pre-synthesized Ag nanoparticles-polyvinylpyrrolidone (AgNPs-PVP) were used to reduce the aryldiazonium tetrachloroaurate(III) salt in water. TEM images and EDS elemental analysis showed the formation of spherical Au–Ag NPs with sizes of 12.8 ± 4.9 nm and 25.6 ± 14.4 nm for corresponding Au–Ag ratios and termed as Au0.91Ag0.09 and Au0.79Ag0.21, respectively, with different concentrations of the gold precursor. The hydrodynamic sizes measured using dynamic light scattering are 46.4 nm and 74.8 nm with corresponding zeta potentials of − 44.56 and − 25.09 mV in water, for Au0.91Ag0.09 and Au0.79Ag0.21 respectively. Oxidative leachability of Ag ion studies from the starting AgNPs-PVP in 1 M NaCl showed a significant decrease in the plasmon peak after 8 h, indicating the complete dissolution of Ag ions, however, there is enhanced oxidation resistivity of Ag from Au–Ag NPs even after 24 h. Electrochemical studies on glassy carbon electrodes displayed a low oxidation peak in aqueous solutions of 20 mM KCl at 0.16 V and KNO3 at 0.33 V vs. saturated calomel electrode (SCE). We studied the antibacterial activity of Au–Ag alloy nanoparticles against gram-positive Staphylococcus aureus, Staphylococcus epidermidis, Enterococcus faecalis, and gram-negative Escherichia coli, Salmonella typhimurium, and Pseudomonas aeruginosa. Our findings demonstrated superior antibacterial activity of Au–Ag NPs compared with AgNPs-PVP. Moreover, the nanoparticles inhibited the S. epidermidis biofilm formation.

Recently, microplastics (MPs) became a big name in the world since their presence in bodies of different species, environmental media, and even in bottled drinking water was frequently reported. Several studies reported MPs’ potential threat to health of humans, animals and the ecosystem. Therefore, it is of great importance to develop reliable technologies for removing MPs in the environment. Advanced oxidation processes (AOPs) are widely studied and applied for the decomposition of different refractory contaminants in the environment. Because reactive oxygen species produced in AOPs could effectively degrade many pollutants, several AOPs were applied for MPs decomposition. Homogeneous and heterogeneous AOPs, including UV photolysis, UV/H2O2, O3, UV/visible light-induced photocatalysis, heat activated PS and PMS, and plasma, could effectively decompose various types of MPs with different sizes. However, the decomposition mostly occurred on the surface of MPs even though several studies reported complete removal of MPs. Interestingly, several studies demonstrated that treated MPs could become pollutant carriers for animals and human beings by adsorbing contaminants in the environment. However, a limited number of studies on MPs removal by AOPs are available and only few types of AOPs are recently studied even though current studies demonstrated the potential of AOPs for complete MPs removal. Therefore, more effort must be put into investigating different AOPs for complete removal of MPs in the environment. AOPs will play a key role for MPs removal in the environment in the near future, definitely.

Compounds with antimicrobial activity have gained much attention in research due to the outbreak of coronavirus disease 2019 (COVID-19). Quaternary ammonium salts (QASs) are an emerging group of antibacterial agents that are used as disinfectants. Many studies have been carried out involving the applications of QASs as antifouling agents for the inhibition of biofilm growth on medical implants and antibacterials on surfaces and in an aquatic environment. In investigating the antibacterial activity of QASs, we addressed the structure-activity relationship and the physicochemical factors. This review is focused on the fine-tuning of the chemical structures of QASs for their applications as wide antibacterial agents.