Chitosan crosslinked with glutaraldehyde or oxidised dextran was studied as a potential scaffold material in tissue engineering for cartilage regeneration. By mixing two solutions of both components it became a gel, which was frozen. After lyophilisation a scaffold was generated with interconnected pores with diameters ranging between 120–350 μm. The mechanical properties (yielding point, elastic and viscous moduli), absolute porosity, pore morphology were determined depending on the ratio of chitosan to crosslinker. ATDC5 (murine cell line) and bovine articular chondrocytes (primary cells) were cultured for 14 days on the scaffolds. Cultivation with ATDC5 cells and bovine chondrocytes showed no negative influence of glutaraldehyde on cell vitality and growth.

Alloys based on titanium or cobalt have been used as implant materials for decades with good success. Because of their natural oxide layer these alloys reveal good corrosion behaviour. In contact with physiological solution metal release takes place, which can cause inflammation. Coatings can improve the corrosion behaviour In this study Ti6Al4V and Co28Cr6Mo alloys, which are frequently used as implant materials, were tested. Polished discs of these alloys and polished discs, which were coated with TiO2-layers by sol-gel chemistry, were compared regarding their corrosion behaviour and metal ion releasing. The releasing of Al, V, Ti, Co, Cr and Mo was quantified by ICP-MS analysis. The TiO2-coating reduced the release of all ions except of the Al-ion. Both alloys showed a deviating kinetic of ion releasing. In addition, cell response (cell vitality, cell proliferation, endothelial marker CD31 and actin allocation) of osteoblasts and endothelial cells were investigated.

Alloys based on titanium or cobalt have been used as implant materials for decades with good success. Because of their natural oxide layer these alloys reveal good corrosion behaviour. In contact with physiological solution metal release takes place, which can cause inflammation. Coatings can improve the corrosion behaviour. In this study Ti6Al4V and Co28Cr6Mo alloys, which are frequently used as implant materials, were tested. Polished discs of these alloys and polished discs, which were coated with TiO2-layers by sol-gel chemistry, were compared regarding their corrosion behaviour and metal ion releasing. The releasing of Al, V, Ti, Co, Cr and Mo was quantified by ICP-MS analysis. The TiO2-coating reduced the release of all ions except of the Al-ion. Both alloys showed a deviating kinetic of ion releasing. In addition, cell response (cell vitality, cell proliferation, endothelial marker CD31 and actin allocation) of osteoblasts and endothelial cells were investigated.