P3HT:PCBM blends applied as active layers for bulk heterojunction organic solar cells generally show unstable morphologies upon prolonged thermal annealing, severely limiting the lifetime of the devices. As such, the thermodynamic instability of the blend is a limiting factor in the overall performance of organic photovoltaics, and a strong disadvantage in the fierce competition with other photovoltaic technologies. This paper shows whether different blend preparation conditions and intrinsic structural changes in the side chains of poly(3-alkylthiophene) (P3AT) derivatives can influence the thermal stability of the resulting solar cells. A combination of Bright Field Transmission Electron Microscopy (BFTEM) and the analysis of Selected Area Electron Diffraction (SAED) patterns revealed that the investigated preparation conditions do not really affect the thermal stability, whereas the introduction of a small ratio (10%) of specific functional moieties in the side chains of random P3AT copolymers does improve the thermal stability significantly. It was demonstrated that demixing of the blend components upon prolonged thermal annealing is strongly delayed in the functionalized P3AT:PCBM blends. The enhanced thermal stability was confirmed by in-situ monitoring of the short circuit current of organic solar cells based on the respective active layers. The introduction of functionalized side chains hence represents an attractive approach to increase the operational stability of organic photovoltaics based on the bulk heterojunction concept.

The introduction of functional moieties in the donor polymer (side chains) offers a potential pathway toward selective modification of the nanomorphology of conjugated polymer:fullerene active layer blends applied in bulk heterojunction organic photovoltaics, pursuing morphology control and solar cell stability. For this purpose, two types of poly(3-alkylthiophene) random copolymers, incorporating different amounts (10/30/50%) of ester-functionalized side chains, were efficiently synthesized using the Rieke method. The solar cell performance of the functionalized copolymers was evaluated and compared to the pristine P3HT:PCBM system. It was observed that the physicochemical and opto-electronic characteristics of the polythiophene donor material can be modified to a certain extent via copolymerization without (too much) jeopardizing the OPV efficiency, as far as the functionalized side chains are introduced in a moderate ratio (<30%) and that preference is given to side chains with a small molar volume. A range of complementary techniques – UV–Vis spectroscopy, (modulated temperature) differential scanning calorimetry, transmission electron microscopy and X-ray diffraction analysis – indicated that variations in polymer crystallinity, while maintaining a high level of regioregularity, are probably the main factor responsible for the observed differences.

We focus upon the role of interfacial energetics and morphology in influencing the separation of CT states into dissociated charge carriers. In particular, we undertake transient optical studies of films comprising regioregular poly(3-hexylthiophene) (P3HT) blended with a series of perylene-3,4:9,10-tetracarboxydiimide (PDI) fullerene electron acceptors. For the PDI film series, we observe a close correlation between the PDI electron affinity and the efficiency of charge separation. This correlation is discussed in the context of studies of charge photogeneration for other organic donor/acceptor blend films, including other polymers, blend compositions, and the widely used electron phenyl-C61-butyric acid methyl ester(PCBM). Furthermore, we compare the charge recombination dynamics observed in films comprising P3HT blended with three fullerene derivatives: PCBM and two alternative pyrazolinofullerenes. Transient absorption data indicate that replacement of PCBM with either of the pyrazolinofullerene derivatives results in a transition from nongeminate to monomolecular (geminate) recombination dynamics. We show that this transition cannot be explained by a difference in interfacial energetics. However, this transition does correlate with nanomorphology data that indicate that both pyrazolinofullerenes yield a much finer phase segregation with correspondingly smaller domain sizes than observed with PCBM. Our results therefore provide clear evidence of the role of nanomorphology in determining the nature of recombination dynamics in such donor/acceptor blends. (C) 2012 Society of Photo-Optical Instrumentation Engineers (SPIE). [DOI: 10.1117/1.JPE.2.021001]

Conjugated copolymer derivatives of poly[2-methoxy-5-(3',7'-dimethyloctyloxy)-1,4-phenylenevinylene] (MDMO-PPV) and poly(3-hexylthiophene) (P3HT) containing 10% of alkyne functionalities in the side chains have been prepared using the sulfinyl precursor route and the Rieke method, respectively. With the aim of expanding the absorption range of these conjugated polymers for their use in bulk heterojunction (BHJ) polymer:fullerene solar cells, appropriate phthalocyanine (Pc) molecules have been covalently bound through a post-polymerization "click chemistry" reaction between the alkyne functionalities in the side chains of the copolymers and a Pc functionalized with an azide moiety. The resulting poly(p-phenylenevinylene)-Pc (PPV-Pc) material holds a 9 mol% content of Pcs, while the polythiophene-Pc material (PT-Pc) contains a 8 mol% of Pc-functionalization in the side chains. As expected, the presence of the Pc contributes to the extension of the absorption up to 700 nm. BHJ solar cells have been prepared using PPV-Pc and PT-Pc materials in combination with PCBM. Although the Pc absorption contributes to the generation of photocurrent, the overall power conversion efficiencies (PCE) obtained from these cells are lower than those obtained with BHJ P3HT:PCBM (1:1) and MDMO-PPV:PCBM (1:4) solar cells. A plausible explanation could be the moderate solubility of the PPV-Pc and PT-Pc materials that limits the processing into thin films.

The efficiency of polymer - metal oxide hybrid solar cells depends critically on the intimacy of mixing of the two semiconductors. The effect of side chain functionalization on the morphology and performance of conjugated polymer:ZnO solar cells is investigated. Using an ester-functionalized side chain poly(3-hexylthiophene-2,5-diyl) derivative (P3HT-E), the nanoscale morphology of ZnO:polymer solar cells is significantly more intimately mixed compared to ZnO:poly(3-hexylthiophene-2,5-diyl) (ZnO:P3HT), as evidenced experimentally from a 3D reconstruction of the phase separation using electron tomography. Photoinduced absorption reveals nearly quantitative charge generation for the ZnO:P3HT-E blend but not for ZnO:P3HT, consistent with the results obtained from solving the 3D diffusion equation for excitons formed in the polymer within the two experimental ZnO morphologies. For thin ZnO:P3HT-E active layers (similar to 50 nm) this yields a significant improvement of the solar cell performance. For thicker cells, however, the reduced hole mobility and a reduced percolation of ZnO pathways hinders charge carrier collection, limiting the power conversion efficiency.

In this paper, we compare the charge recombination dynamics observed in films comprising poly(3-hexylthiophene) blended with three fullerene derivatives: PCBM and two alternative pyrazolinofullerenes. Transient absorption data indicate that replacement of PCBM with either of the pyrazolinofullerene derivatives results in a transition from bimolecular to monomolecular (geminate) recombination dynamics. We show that this transition cannot be explained by a difference in interfacial energetics. However, this transition does correlate with nanomorphology data which indicate that both pyrazolinofullerenes yield a much finer phase segregation, with correspondingly smaller domain sizes, than observed with PCBM. Our results therefore provide clear evidence of the role of nanomorphology in determining the nature of recombination dynamics in such donor/acceptor blends.

A set of novel regioregular poly(3-hexylthiophene)-based random copolymers containing varying ratios of ester functionalized alkyl side chains were synthesized using the Rieke method. The percentage of functionalized side chain varied between 10 and 50 mol% for each copolymer. Using post-polymerization reactions, the ester functions in the alkyl side chain were hydrolyzed to yield an alcohol or acid group. These groups are available for further functionalization reactions, so a wide variety of secondary functionalities may be covalently attached to the conjugated polymer. The copolymers were applied in polymer: fullerene bulk heterojunction solar cells (BHJSCs) with [6,6]-phenyl-C-61-butyric acid methyl ester (PCBM) as electron acceptor. The influence of side-chain functionalities on absorption, device performance and layer morphology depends on the ratio and nature of the functionalized side chains. For a 9/1 copolymer, containing 10% of functionalized side chains, behaviour and efficiency in BHJSCs comparable to P3HT:PCBM solar cells were observed.