PURPOSETo investigate the effect of roughness and drying time of dentin as well as the number of coats of a self-adhesive composite-cement primer on the bond strength of self-adhesive composite cement.MATERIAL AND METHODSSixty human teeth were prepared and assigned to 12 groups (n = 5), according to three experimental factors: 1) dentin surface roughness, rough or fine, as achieved by 250- and 600-grit silicon carbide papers, respectively; 2) dentin wetness based on air-drying time (5 or 10 s); and 3) the self-adhesive composite-cement primer applications (no-coat, 1-coat, and 2-coat). Composite resin blocks were made with hybrid composite resin (M1 GraceFil) and cemented with G-CEM ONE (both GC). Cement-dentin sticks (12) were prepared, and the microtensile bond strength (μTBS) test was performed. Failure modes were observed with a stereomicroscope (40X), and bonding interfaces were evaluated with confocal laser scanning microscopy (CLSM). Statistical analysis was performed using three-way ANOVA and Tukey's post-hoc comparisons test (α = 0.05).RESULTSDentin roughness (250-grit > 600-grit, p = 0.000), drying time (5-s drying > 10-s drying, p = 0.000), and primer application (no-coat < 1-coat = 2-coat, p = 0.000) had significant effects on bond strength. These factors also showed significant interactions with each other (p = 0.003). The highest μTBS (31.8 ± 3.1 MPa) was observed in the 1-coat/fine roughness/10-s drying group and the lowest μTBS (13.4 ± 2.7 MPa) in the no-coat/coarse roughness/5-s drying group. CLSM showed higher penetration of cement in the primer-coated groups compared to that in the no-coat groups.CONCLUSIONBond strength between the self-adhesive composite cement and dentin was higher in the fine-roughness dentin group than in the coarse-roughness dentin group, and in the 5-s drying group compared to the 10-s drying group. Applying a primer to dentin improved bond strength of the self-adhesive composite cement.

The treatment of teeth with severely calcified canals is a diffi-cult procedure for clinicians. Procedural accidents such as drill path deviation or perforation of the root canal often occur. 3D-printed directional guides made using CBCT and CAD/ CAM can help the clinician to accurately drill in the original root canal direction. Furthermore, chairside operating times and excessive loss of tooth structure are reduced, and the risk of perforation is avoided. The present case report describes two cases of calcified root canals with path deviations that were retreated utilizing a guided endodontic technique.