A method is presented for synthesizing core-shell nanoparticles with a magnetic core and a porous shell suitable for drug delivery and other medical applications. The core contains multiple γ-Fe2O3 nanoparticles (∼15 nm) enclosed in a SiO2 (∼100-200 nm) matrix using either methyl (denoted TMOS-γ-Fe2O3) or ethyl (TEOS-γ-Fe2O3) template groups. Low-temperature Mössbauer spectroscopy showed that the magnetic nanoparticles have the maghemite structure, γ-Fe2O3, with all the vacancies in the octahedral sites. Saturation magnetization measurements revealed that the density of γ-Fe2O3 was greater in the TMOS-γ-Fe2O3 nanoparticles than TEOS-γ-Fe2O3 nanoparticles, presumably because of the smaller methyl group. Magnetization measurements showed that the blocking temperature is around room temperature for the TMOS-γ-Fe2O3 and around 250 K for the TEOS-γ-Fe2O3. Three dimensional topography analysis shows clearly that the magnetic nanoparticles are not only at the surface but have penetrated deep in the silica to form the core-shell structure.

A route for synthesizing monodisperse magnetic nanocrystallites of maghemite, [Formula: see text]-Fe2O3, with various sizes has been revisited. A systematic investigation of three [Formula: see text]-Fe2O3 nanocrystalline samples by different techniques has been performed to characterize their size-dependent magnetic properties. Zero-field-cooled and field-cooled magnetization measurements reveal that the superparamagnetic blocking temperatures are around 230 K, 170 K, and 50 K for the 15.0 nm, 11.8 nm, and 6.1 nm nanocrystallites, respectively. Low-temperature Mössbauer spectra show that all three nanocrystallites have the maghemite structure with all the vacancies in the B-sites. Furthermore, detailed analysis shows that there are more vacancies on the B-sites for the 6.1 nm nanocrystallites compared to 0.33 for the bulk maghemite.