In this study, the method of process design for side forming of a tooth part used for a component of automobile transmission was suggested using FE-simulations. To develop the side forming for the tooth part, in this paper, the shape factors of B.T.Pin was considered as design parameters. The shape factors of B.T.Pin were selected to be the round of pin, reinforced angle and reinforced length. Based on FE simulation results, appropriate shape factor without causing any defects was selected. In addition, to increase the strength of pin, the combination of shape factor having minimum stress after side forming was selected using FE-simulation. In addition, with design of a die set, cold side forming of the tooth part was experimented to estimate effectiveness of the designed B.T.Pin. From experiments, it was found that the tooth part with complete formation of the tooth was obtained without making any forming defects and punch fracture.

In this study, powder compaction of AZO (alumina doped zinc oxide) powder was performed with a MTS 810 test system using a cylindrical die having a diameter of 10mm. Pressure-density curves were measured based on the load cell and displacement of the punch. The AZO powder compacts with various densities were formed to investigate the mechanical properties such as fracture stress of the AZO powder as a function of the compact density. Two types of compression tests were conducted in order to estimate the fracture stress using different loading paths: a diameteral compression test and a uniaxial compression test. The pressure-density curves of the AZO powder were obtained and the fracture stress of the compacted powders with various densities was estimated. The results show that the compact pressure dramatically increases as the density increases. Based on the experimental results, calibration of the modified Drucker-Prager/Cap model of the AZO powder for use in FE simulations was developed.