The Earth Observing System Microwave Limb Sounder measures several atmospheric chemical species (OH, HO/sub 2/, H/sub 2/O, O/sub 3/, HCl, ClO, HOCl, BrO, HNO/sub 3/, N/sub 2/O, CO, HCN, CH/sub 3/CN, volcanic SO/sub 2/), cloud ice, temperature, and geopotential height to improve our understanding of stratospheric ozone chemistry, the interaction of composition and climate, and pollution in the upper troposphere. All measurements are made simultaneously and continuously, during both day and night. The instrument uses heterodyne radiometers that observe thermal emission from the atmospheric limb in broad spectral regions centered near 118, 190, 240, and 640 GHz, and 2.5 THz. It was launched July 15, 2004 on the National Aeronautics and Space Administration's Aura satellite and started full-up science operations on August 13, 2004. An atmospheric limb scan and radiometric calibration for all bands are performed routinely every 25 s. Vertical profiles are retrieved every 165 km along the suborbital track, covering 82/spl deg/S to 82/spl deg/N latitudes on each orbit. Instrument performance to date has been excellent; data have been made publicly available; and initial science results have been obtained.

During ground based life testing of a Microwave Limb Sounder (MLS) Antenna Actuator Assembly (AAA) ball-screw assembly, lubricant darkening and loss were noted when approximately 10% of required lifetime was completed. The MLS-AAA ball screw and nut are made from 17-4 PH steel, the nut has 440C stainless steel balls, and the assembly is lubricated with a Pennzane (R) formulation containing a three weight percent lead naphthenate additive. Life tests were done in dry nitrogen at 50 degrees C. To investigate the MLS-AAA life test anomaly, Spiral Orbit Tribometer (SOT) accelerated tests were performed. SOT results indicated greatly reduced relative lifetimes of Pennzane (R) formulations in contact with 17-4 PH steel compared to 440C stainless steel. Also, dry nitrogen tests yielded longer relative lifetimes than comparable ultrahigh vacuum tests. Generally, oxidized Pennzane (R) formulations yielded shorter lifetimes than nonoxidized lubricant. This study emphasizes surface chemistry effects on the lubricated lifetime of moving mechanical assemblies.

During ground based life testing of a Microwave Limb Sounder (MLS) Antenna Actuator Assembly (AAA) ball-screw assembly, lubricant darkening and loss w ere noted when approximately 10% of required lifetime was completed. The MLS-AAA ball screw and nut are made from 17-4 PH steel, the nut has 440C stainless steel balls, and the assembly is lubricated with a Pennzane ® formulation containing a three weight percent lead naphthenate additive. Life tests were done in dry nitrogen at 50°C. To investigate the MLS-AAA life test anomaly, Spiral Orbit Tribometer (SOT) accelerated tests were performed. SOT results indicated greatly reduced relative lifetimes of Pennzane ® formulations in contact with 17-4 PH steel compared to 440C stainless steel. Also, dry nitrog en tests yielded longer relative lifetimes than compar able ultrahigh vacuum tests. Generally, oxidized Pennza ne® formulations yielded shorter lifetimes than non- oxidized lubricant. This study emphasizes surface chemistry effects on the lubricated lifetime of mov ing mechanical assemblies.