Polymer-derived SiC and SiOC aerogels have been synthesized and characterized both from the microstructural point of view and as sorbent materials for removing organic dyes (Methylene Blue, MB, and Rhodamine B, RB) from water solutions. Their adsorbent behavior has been compared with a polymer-derived SiC foam and a commercial mesoporous silica. The aerogels can efficiently remove MB and RB from water solution and their capacity is higher compared to the SiC foams due to the higher surface area. The SiOC aerogel remains monolithic after the water treatment (allowing for an easy removal without the need of a filtration step) and its maximum capacity for removing MB is 42.2 mg/g, which is higher compared to the studied mesoporous silica and many C-based porous adsorbents reported in the literature. The reason for this high adsorption capacity has been related to the unique structure of the polymer-derived SiOC, which consists of an amorphous silicon oxycarbide network and a free carbon phase.

The presence of residual color in treated textile wastewater above the regulation limits is still a critical issue in many textile districts. Innovative, polymer-derived ceramics of the Si–C–O system were here synthesized in order to obtain porous nanocomposite materials where a free carbon phase is dispersed into a silicon carbide/silicon oxycarbide network. The sorbents were comprehensively characterized for the removal of two model water-soluble dyes (i.e., the cation methylene blue and the zwitterion rhodamine B). Adsorption is very rapid and controlled by intra-particle and/or film diffusion, depending on dye concentration. Among the nanocomposites studied, the SiOC aerogel (total capacity about 45 mg/g, is easily regenerated under mild treatment (250 °C, 2 h). Adsorption of dyes is not affected by the matrix composition: removals of 150 mg/L methylene blue from river water and simulated textile wastewater with high content of metal ions (2–50 mg/L) and chemical oxygen demand (800 mg/L) were higher than 92% and quantitative for a dye concentration of 1 mg/L.

Iron oxide clusters were incorporated into amino-functionalized SBA-15 in order to obtain a magnetically recoverable adsorbent. The physical-chemical properties of the material were characterized by FE-SEM, STEM, XRD, TGA, XPS, FT-IR and acid-base titration analysis. Iron oxide nanoparticles were uniformly dispersed into the pore of mesoporous silica and that the adsorbent is characterized high specific surface area (177 m(2)/g) and accessible porosity.The sorbent was successfully tested for the removal of glyphosate in real water matrices. Despite the significant content of inorganic ions, a quantitative removal of the contaminant was found. The complete regeneration of the sorbent after the adsorption process through diluted NaOH solution was also proved. (C) 2017 Elsevier B.V. All rights reserved.

Glyphosate is a worldwide-used herbicide occurring in many monitoring campaigns. Efficient technologies are currently unavailable for glyphosate removal from waters. In this work, a SBA-15 mesoporous silica-based material (Fe-NH2-SBA-15) was synthesized and studied for the adsorption of glyphosate from waters. In order to promote specific interactions between the sorbent and glyphosate via phosphoric group, iron oxide nanoparticles were encapsulated and a surface functionalization with (3-aminopropyl)triethoxysilane was accomplished. The adsorption of glyphosate on Fe-NH2-SBA-15 was investigated as a function of (i) pH, (ii) ionic strength (I), and (iii) adsorbate to adsorbent ratio (C), using a two-level, three-factor experimental design. The experimental design allowed for understanding the effect of the abovementioned variables and for proposing experimental conditions for quantitative removal (pH = 2.1, I = 1⋅10−2 M and C = 0.35) under both batch and dynamic conditions. Interaction mechanism between glyphosate and Fe-NH2-SBA-15 sorbent was elucidated by studying the adsorption behavior of sorbents derived from the intermediate stages of synthesis and by desorption tests. Fe-NH2-SBA-15 sorbent can be quantitatively regenerated by 12.5 mM NaOH, and can be reused at least for five adsorption/desorption cycles. Quantitative removal of glyphosate from inlet and effluent wastewaters from a wastewater treatment plant is shown.

A process is described for preparing light weight and low cost polymer-derived silicon carbide foams by impregnation with polymeric precursor and polyurethane foam, followed by pyrolysis in inert atmosphere. Scanning electron microscopy showed that the resultant silicon carbide foams had a fully open and interconnected porous structure with dense struts. The suitability of these silicon carbide foams for the adsorption of non-steroidal anti-inflammatory drugs and their metabolites was studied. The results showed that silicon carbide foams adsorbed the target compounds and adsorption capacity increases with increasing the contact time between the foam and the analytes investigated.