Two model drug eluting stents of poly(lactic acid) (PLA)/everolimus and poly(ethylene vinyl alcohol) copolymer (EVAL)/everolimus have been investigated using complementary surface analysis techniques including AFM, XPS, and ATR-IR to assess their structure and its relation to drug release. Different surface morphologies were observed for these stents, with phase separation evident on the PLA coating and a homogeneous system for the EVAL-based coating. This indicates a potentially different drug distribution for the different stents, although both showed a surface enrichment of the drug compared to the bulk. Dissolution studies for PLA/everolimus stents showed an immediate loss of drug from the surface as well as a longer term polymer matrix erosion. The EVAL/everolimus stent also displayed a loss of drug from its surface, but an intact surface after 28 days in dissolution media. These data are discussed in relation to the different release mechanisms occurring in the stents.

Localized atomic force microscopy (AFM) force analysis on poly(lactic acid) (PLA) and poly(lactic acid)/everolimus coated stents has been performed under ambient conditions. Similar Young's modulus were derived from both PLA and PLA/everolimus stent surface, namely 2.25+/-0.46 and 2.04+/-0.39GPa, respectively, indicating that the drug, everolimus does not significantly effect the mechanical properties of PLA up to a 1:1 (w/w) drug loading. Temperature controlled force measurements on PLA only coated stents in air and in a 1% Triton surfactant solution allowed the glass transition temperature (T(g)) of the polymer to be determined. A significant drop of the Young's modulus in solution was observed at 36 degrees C, suggests that in vivo the T(g) of the polymer is below body temperature. The possible consequences on drug release and the mechanisms by which this may occur are considered.