Functionalization of GO with an amphiphilic block copolymer is designed with an aim to enhance its biocompatibility, however, long copolymer chains can screen the blade effect of GO to sacrifice its antimicrobial activities. To solve this problem, low molecular weight of poly(ethylene glycol) (PEG), poly(3-hydroxybutyrate-co3-hydroxyvalerate) (PHBV) and their block copolymer were respectively introduced onto GO via an isophorone diisocyanate modified GO as a intermediate, followed by a solvent evaporation of an oil-in-water emulsion treatment (SE treatment) to induce block copolymer into polymer micelle via phase separation to refresh the sharp edges of GO. Block copolymer modified GO possessed similar dispersibility and stability to PEG modified GO, and even higher loading capacity of the hydrophobic drug than PHBV modified GO, illustrating its superior properties to homopolymer. PEG, PHBV and their block copolymer modified GO were nontoxic towards ATDC5 cells while cultured for 3 days and compatible with erythrocytes within 8 h. SE treatment enhanced greatly the loading capacity of the hydrophobic drug and the accumulative release reached 91.3% within 24 h. The inhibition zone of the block copolymer modified GO was 14.1 mm and 14.8 mm against E. coli and S. aureus, comparable to that of PEG modified GO. The bacterial reduction rate of the copolymer micelle modified GO was 87.1% and 82.7% towards E. coli and S. aureus, much greater than that of PEG, PHBV and their block copolymer modified GO at a concentration of 1 mg/mL. The antibiofilm capacity of the copolymer micelle modified GO were equal to that of PEG modified, demonstrating its great promise in tissue engineering application for repair of infected tissue defects.

Biomedical implants-associated bacterial infections have become a major threat to human health. Therefore, it is meaningful to develop new antibacterial strategies to solve this problem. In this study, we conjugated acetylated lentinan (AceLNT) with α-terpineol (AceLNT-g-α-ter), a highly effective natural antibacterial compound, to constitute a novel AceLNT-g-α-ter membrane (AceLNT-g-α-terM). Compared with AceLNT membrane (AceLNTM), the adhesion amount of E. coli and P. aeruginosa in AceLNT-g-α-terM decreased by 80% and 85% after 7 d incubation in fluid bacterial medium. Moreover, the number of E. coli and P. aeruginosa biofilm on AceLNT-g-α-terM surface decreased by 70% and 71%. At the meanwhile, α-terpineol grafting modification of AceLNT had limited effect on its stimulating activity on macrophages and had no more cytotoxicity. In summary, our study firstly confirmed that AceLNT-g-α-terM could effectively inhibit gram-negative bacteria adhesion and biofilm formation, and provided a novel strategy for preventing infection of biomedical implants.

A magnetic-pH dual responsive drug delivery system was prepared for antibacterial therapy to reduce the side effects on nonpathological cells or tissues. Iron oxide (Fe3O4) core was surface-functionalized with silane coupling agents to link β‑cyclodextrin (β-CD) (CDMNP), and a polypseudorotaxanes shell where polyethyleneglycol chains threaded much CD molecules was further prepared on the magnetic Fe3O4 core (CDMNP-PEG-CD) to enhance loading capacity of roxithromycin (ROX). CDMNP-PEG-CD with a hydrodynamic diameter of ~168 nm was cytocompatible, superparamagnetic, magnetic-responsive and stable for 180 min of storage. No significant interaction with serum albumin was shown for the nanocomposites. The in vitro release from ROX-loaded CDMNP-PEG-CD nanocomposites was about 76% of total drug within 30 min at pH 1.0, 1.6-fold of that at pH 7.4 and 2-fold of that at pH 8.0, presenting pH-responsive drug release behaviors. The nanocomposites showed positive antibacterial activity against both E. coli and S. aureus based on an agar diffusion method. The antibacterial activity of the nanocomposites was more sensitive against E. coli than S. aureus, and the inhibition halo against E. coli was 85% more than that of Fe3O4. CDMNP-PEG-CD nanocomposites allowed for the localization and fast concentration of hydrophobic drugs, providing a broad potential range of therapeutic applications.

Cell-loaded carboxymethylcellulose (CMC) microspheres were generated via a flow focusing microfluidic device, with a final aim to obtain viable ATDC5 aggregates with sustained proliferation capacity. We synthesized various CMC with phenolic groups (CMC-Ph) and demonstrated that high CMC-Ph molecular weight, high CMC-Ph concentration (>0.8g/ml) or long culturing period had obvious inhibition effect on ATDC5 proliferation, but low horseradish peroxidase concentration (HRP, <0.4mg/ml) did not. CMC-Ph gels being obtained through HRP/H2O2 reaction showed an enhancing strength and decreasing break stain as the molecular weight of CMC-Ph increased, along with a decreasing gelation time. The microfluidics-based synthesis of cell-loaded microspheres with great design flexibilities was achieved using CMC-Ph with weight-average molecular weight of 1.0 x 10(5). ATDC5 cells were viable up to 41 days of culture and proliferated gradually with increasing culture time. High cell density in CMC-Ph solution and high fetal bovine serum concentration in culture medium were prone to forming cell aggregates. Isolated cells from the microspheres showed the typical spherical morphology of undifferentiated ATDC5. Therefore, CMC-Ph microspheres might be used as cell aggregates depots to study cell-cell or cell-biomaterials functions for tissue engineering applications. [GRAPHICS] .