Hyperbranched polyethyleneimines were modified with methacrylated fluorosurfactants and aliphatic epoxides to provide a library of macromolecules with controlled chain ends and residual amine functionality. These materials were co-dissolved with a thermoplastic polyurethane-ether and the blends were subsequently deposited as films cast from solution. The surface chemistry of the cast films was determined using angle resolved X-ray photoelectron spectroscopy (AR-XPS) and Rutherford backscattering spectroscopy (RBS). Experimental results indicate that the modified hyperbranched polymers (HBPs) concentrate at the air–polymer interface. Furthermore, HBPs that were complexed to polyoxometalates (POMs) using electrostatic interactions also exhibited surface segregation in cast polymer films, resulting in ca. 10-fold increase of metal at the film surface relative to the known bulk concentration. Results from XPS and RBS examination of the films are consistent with surface segregation of the HBP–POM hybrids, exhibiting increased metal, fluorine, and nitrogen content near the surface of the film, as well as significant changes in wetting behavior. This study indicates that modified HBPs may be used to selectively transport inorganic species such as polyoxometalates to polymer film surfaces.

In this work, polyamide (Nylon 6) fibers and films were treated under atmospheric pressure glow discharges (APGD) and the effects on the morphology and chemistry of the material were studied. The fibers were plasma treated with N-2, C2H2 in He for (0.6-9.6) s at a frequency of 90 kHz, leading to the functionalization of the surface through the addition of new reactive chemical groups such as -COOH and -OH and changing the energy, chemical composition and wettability of the surface.Surface characteristics were examined via contact angle measurements, XPS, and SEM. Wettability tests revealed the improvement of the hydrophilic character of the surface as the water contact angle measured after the plasma treatments significantly decreased. The corresponding changes of the total surface energy were evaluated with a dynamic contact angle analysis system revealing a significant increase due to the exposure that can be mainly attributed to the increase of its polar component. Preliminary XPS results show a significant increase in oxygen content with the addition of carboxylic and hydroxylic groups and a decrease in the carbon content of the surface. Most importantly, the plasma modified nylon fibers and films exhibit a stable wetting behavior, even for weeks after being treated, suggesting that it is a promising technique to minimize aging phenomena. (c) 2006 Published by Elsevier B.V.