From aqueous slurries containing SiC powder coated with nano-scaled carbon black, green bodies were prepared by slip casting. On slip cast green bodies the densification, microstructural development and mechanical properties were investigated. Depending on the sintering temperature and boron carbide content samples with different relative densities between 0.90 and 0.988 were obtained after pressureless sintering. In all samples a homogeneous microstructure (distribution of the residual pores and grain morphology) was observed. Due to this homogeneity the sintered samples showed high amount of fracture strength of about 500 MPa, even at large residual porosities of 10 %. The thermal shock resistance of samples with different porosities measured by water quenching revealed the critical temperature difference to be around 700 K.

La synthese des nanoparticules ceramiques peut se faire de deux facons differentes qui produisent des particules sans agglomerats et d'une qualite de traitement de surface < 10 nm. La premiere est un processus continu de reaction hydro-thermique qui modifie de facon ciblee la surface, la seconde est un nouveau procede mecano-chimique de moulage. Sur ces bases, on a developpe plusieurs procedes ceramiques, comme par exemple le procede de la feuille coulee pour produire des membranes ceramiques ultra fines dont la taille des pores peut descendre jusque sans le domaine nanometrique, du SIC a grande conductibilite, du moulage a microinjection par utilisation de micro-particules, des revetements catalytiques (d'une technologie nouvelle a base de nanoparticules) ou la production de nanocomposites constitues de nanoparticules ceramiques avec une matrice polymere. D'autres domaines sont par exemple le revetement optiques, les photo-catalyseurs et les utilisations en Sciences de la Vie. A partir de cela se sont crees des technologies qui ont permis la fabrication de plus de quarante nouveaux produits dans les cinq dernieres annees.