To date, the outcomes of cartilage repair have been inconsistent and have frequently yielded mechanically inferior fibrocartilage, thereby increasing the chances of damage recurrence. Implantation of constructs with biochemical composition and mechanical properties comparable to natural cartilage could be advantageous for long-term repair. This study attempted to create such constructs, in vitro, using tissue engineering principles. Bovine synoviocytes were seeded on nonwoven polyethylene terephthalate fiber scaffolds and cultured in chondrogenic medium for 4 weeks, after which uniaxial compressive loading was applied using an in-house bioreactor for 1 h per day, at a frequency of 1 Hz, for a further 84 days. The initial loading conditions, determined from the mechanical properties of the immature constructs after 4 weeks in chondrogenic culture, were strains ranging between 13% and 23%. After 56 days (sustained at 84 days) of loading, the constructs were stained homogenously with Alcian blue and for type-II collagen. Dynamic compressive moduli were comparable to the high end values for native cartilage and proportional to Alcian blue staining intensity. We suggest that these high moduli values were attributable to the bioreactor setup, which caused the loading regime to change as the constructs developed, that is, the applied stress and strain increased with construct thickness and stiffness, providing continued sufficient cell stimulation as further matrix was deposited. Constructs containing cartilage-like matrix with response to load similar to that of native cartilage could produce long-term effective cartilage repair when implanted.

ObjectivesTo compare fatigue resistance and fracture mode of metal-ceramic crowns with all-ceramic crowns containing yttria tetragonal zirconia polycrystal (Y-TZP) frameworks under compressive cycling loading in water.MethodsTwenty specimens of ivory were randomized and individually prepared to receive anatomically shaped metal-ceramic (n=10) or veneered Y-TZP all-ceramic crowns (n=10). All steps in production were equivalent to clinical situations. Resistance to fatigue fracture was tested under compressive cyclic loading using a universal testing machine, with a loading frequency of 12Hz using a spherical tungsten carbide indenter (6mm diameter) in distilled water. The maximum compressive load was increased as the number of cycles increased (600,000 cycles at 400N, 200,000 cycles at 600N, 200,000 cycles at 800N and 200,000 cycles at 1000N). The specimens were inspected after each loading sequence for initial failures such as infractions. Final failure was considered as any loss of material which automatically ended the test and the number of cycles until final failure was recorded. Fractographic analysis of the fractured specimens was performed with scanning electron microscopy (SEM).ResultsThe two types of crowns exhibit similar fatigue resistance (P=0.87) to compressive cycling loading under wet conditions. The failure modes as observed with SEM were similar in the two groups and were found in the veneer ceramic, except that three veneered Y-TZP all-ceramic crowns displayed a complete framework fracture.ConclusionsWithin the limitation of this study using simulated oral masticatory function, the results revealed that the fatigue resistance was similar for the two crown types.Clinical significanceIn this study metal-ceramic crowns and veneered Y-TZP all-ceramic crowns showed similar fracture resistance to compressive cycling loading in water. The test conditions were simulating clinical conditions. Thus, the result may predict the long-term clinical performance of these types of crowns.

Introduction To date, success in the repair of articular cartilage has been inconsistent and can result in formation of mechanically inferior fibro-cartilage, thereby increasing the chances of damage recurrence. One possible repair strategy is the implantation of mechanically functional tissue produced in-vitro using tissue engineering. In this study, compressive loading was applied to immature, pre-cultured, cartilage-like constructs with the aim of increasing the constructs’ compressive moduli to reach those of native cartilage.